ALKALI-SILICA REACTION IN SEVERAL UK CONCRETES: THE EFFECTS OF TEMPERATURE AND HUMIDITY ON EXPANSION, AND THE SIGNIFICANCE OF ETTRINGITE DEVELOPMENT --PROCEEDINGS OF THE 7TH INTERNATIONAL CONFERENCE ON CONCRETE ALKALI-AGGREGATE REACTIONS, OTTAWA, CANADA, 1986

T. Jones,A. Poole
Abstract:The effects of temperature and relative humidity on alkali-silica reactive concretes from three UK structures are being investigated in a series of long-term experiments, and interim findings are presented here. Preliminary indications are that temperature has both the opposite and a far more significant effect on expansion behaviour than previously recognised. Expansion rate is initially proportional to temperature, but falls off more rapidly at higher temperatures than at lower temperatures. Maximum expansion is inversely proportional to temperature, and final expansion at lower temperatures may be more than twice that at 38 deg c. The cutoff humidity (defined as that below which expansion due to asr (alkali silica reaction) does not occur) is higher at elevated temperatures, and expansion variability between concretes is most apparent at lower temperatures and higher humidities. Petrological examination of test samples reveals moderate alkali contents but only small quantities of gel, and concretes from one structure contain an abundance of ettringite. In the absence of external sulphate it is concluded that the ettringite formed by recrystallization of primary sulphate minerals, and was stabilised by reaction of the limestone aggregate. This was probably facilitated by asr, and it is proposed that the resulting pressures contributed to concrete distress. The accepted model of alkali-silica reaction is reviewed in the light of these findings. It is proposed that temperature has a direct effect on both reactant transport and aggregate attack processes. Moisture availability is considered fundamental to expansion of the reaction product, but its effect is thought to be modified by temperature which alters the gel structure, and hence its swelling properties. It is observed that other factors may interact with asr to cause deterioration, and that secondary processes may continue after asr is exhausted. The implications of these findings to the management of affected structures are discussed.(a) for the covering abstract of the conference see IRRD 811982.
Chemistry,Engineering,Materials Science
What problem does this paper attempt to address?