Abstract:This study aims to investigate the fatigue crack growth (FCG) behavior of a railway wheel steel, which has undergone inclusion modification through sulfides enveloping oxides. It involves experimental and finite element (FE) investigations, including microstructural and inclusion analysis, mechanical testing (tensile, hardness, fracture toughness, and FCG tests), and FE analysis based on tessellated stress model and fracture mechanics method. The test results reveal that the microstructure of wheel steel remains almost unchanged as the sulfur content increases from 0.002% to 0.008%. However, the inclusion area fraction increases, the average inclusion size decreases, and most of the oxides are modified to be the duplex inclusions in the form of sulfide enveloping oxide. Moreover, the FCG resistance and fracture toughness are improved. The FE analysis results indicate that the tessellated stress around the inclusion, which is caused by the thermal expansion mis-match between inclusions and matrix material, can be reduced by the coverage of hard oxides by soft sulfides. This reduces the driving force of FCG at low Δ K ranges and results in improved FCG resistance. Furthermore, due to the lower driving force of FCG, fatigue cracks in the modified steel are more prone to deflect at cementite lamellas at low Δ K ranges, which leads to a rougher fracture surface. This further improves the FCG resistance by the mechanism of roughness-induced closure. As Δ K increases, FCG is gradually controlled by the remote applied loading, and the influence of the inclusion tends to disappear. In addition, the thermal expansion mis-match between inclusions and matrix material is found to have a more significant effect on FCG of wheel steel than the stiffness mis-match.

Coupled influence of pore defects on the failure site for high-speed railway gearbox material

Cyclic deformation fields interactions between pores in cast high manganese steel

Finite Element Simulation and Fatigue Damage Analysis of High-Speed Train Gearbox Shell Based on Structure and Material Cross-Scale Correlation

Fatigue failure mechanism of high-speed train bearing steel after long-term service

Crack propagation life of high-speed aviation gear

Study on the Influence of Gear Rattling on Pitting Fatigue Failure

Dynamic Characteristics of Gear System Under Compound Fault of Tooth Root Crack and Bearing Outer Ring

The effect of porosity size on the high cycle fatigue life of nickel-based single crystal superalloy at 980 °C

A fatigue life prediction method distinguishing fracture modes for Ni-based single crystal superalloys considering porosity defect

High-cycle fatigue failure analysis of cast Al-Si alloy engine cylinder head

Study of Fatigue Crack Initiation and the Propagation Mechanism Induced by Pores in a Powder Metallurgy Nickel-Based FGH96 Superalloy

A fatigue life prediction approach for porosity defect-induced failures in directed energy deposited Ti-6Al-4V considering crack growth environment

Morphological Feature Simulation of Gear Pitting Debris Based on the Extended Finite Element Method

Crack initiation mechanisms and life prediction of GH4169 superalloy in the high cycle and very high cycle fatigue regime

Analysis of Microporosity-Dependent Fatigue Crack Behavior in Alloy 718 by Using Synchronic Radiation X-Ray CT and FEM

Quantitative Relationship Between Weld Defect Characteristic and Fatigue Crack Initiation Life for High-Cycle Fatigue Property

Fatigue crack growth behavior of railway wheel steel modified by sulfides enveloping oxides inclusions

Zone‐based failure risk assessment of fatigue crack growth caused by initial defects in powder turbine disc

On the Failure Mechanism for High Pressure Die Casting A390 Hypereutectic Alloy in Low Cycle and High Cycle Fatique

Experimental and numerical insights into fatigue crack propagation of railway component with gradient residual stress

Three-dimensional correlation of damage criticality with the defect size and lifetime of externally impacted 25CrMo4 steel