Abstract:Usually, to obtain multicolor upconversion in lanthanides, materials with different codopants, different size, chemical composition or compositional architecture are required. However, designing a material whose emission color can be tuned in-situ by an external stimulus, such as temperature, excitation pulse duration or photoexcitation density, is of great interest for many applications, but still remains a challenge. The possible solution for this issue can be achieved by intentional codoping the luminescent materials with optically active ions which can disturb or compete with other energy transfer processes, and in consequence lead to changes in relative emission intensity, thus the dominant emission color. Here we synthesized and investigated colloidal luminescent Yb3+ and Tm3+ doped NaYF4 nanoparticles which were codoped with optically active Ce3+ ions, whose relative emission intensity ratios between 1D2→3F4 (at 450 nm), 1G4→3H6 (at 475 nm), 1G4→3F4 (at 650 nm), and 3H4→3H6 (at 800 nm) were significantly dependent from external stimulus – namely temperature and/or excitation pulse length. Our results shows two fold increase in 450/800, 470/800 and 650/800 luminescence intensity bands ratios (LIR) only after incorporation of Ce3+ ions to the material, and even three-fold increase in those LIR after changing the excitation conditions (i.e. pulse width). Moreover, temperature dependent luminescence properties revealed relative sensitivity of 4%/K for the 450/800 and 470/800 bands ratio and almost 5.5%/K for the 650/800 band ratio close to 0 °C. By switching to physiological range of temperatures, the thermal sensitivity decreased to around 2%/K for the 450/800 and 470/800 bands ratio and to over 2.5%/K for 650/800 bands ratio, which should be considered as significant values and suitable for temperature sensing in practical applications. It is worth noting that the thermal sensitivity values can be further enhanced by applying different excitation pulse width. The proposed materials allows to tune its emissions as well as thermal properties by changing the dopant concentration or more importantly also in situ, through excitation scheme modifications.

Impacts of Ce3+ doping on temperature sensing characteristics of LuAG: Yb3+/Ho3+ up-conversion fluorescent materials

Improved Temperature Sensing Performance of YAG: Ho3+/Yb3+ by Doping Ce3+ Ions Based on Up-Conversion Luminescence

Enhanced up-conversion luminescence in Na5Y9F32: Ho3+/Yb3+/Eu3+ single crystals by introducing of Gd3+ ions for highly sensitive temperature sensing

High-sensitivity Ratiometric Thermometers of Yb 3+/er 3+/tm 3+Co-Doped LuScO 3 Single Crystal Fibers Based on Non-Thermally Coupled Energy Levels

Optical temperature sensing properties of Tm<SUP>3+</SUP>/Yb<SUP>3+</SUP> co-doped LuAG polycrystalline phosphor based on up-conversion luminescence

Up-Conversion Luminescence and Temperature Sensing of Er 3+ /Yb 3+ Codoped Y 2(1– x %) Lu 2 x % O 3 Solid Solution

High-sensitivity Ratiometric Thermometers of Yb3+/Er3+/Tm3+ Co-Doped LuScO3 Single Crystal Fibers Based on Non-Thermally Coupled Energy Levels

Optical Temperature Sensing Characteristics of Yb3+/Nd3+ Co-Doped YAG Single Crystal Fiber Based on Up-Conversion Luminescence

Selective Enhancement of Green Upconversion Luminescence from NaYF4:Yb, Er Microparticles Through Ga3+ Doping for Sensitive Temperature Sensing

Ultrasonic Spray Pyrolysis Synthesis and Photoluminescence of LuAG:Ce Thin Films

Improvement of upconversion and temperature sensing properties in Ho3+/Yb3+ co-doped Ca0.5Gd(WO4)2 phosphor via incorporation of Bi3+

The influence of Ce3+ codoping on upconversion in nanocrystalline NaYF4:Yb3+,Tm3+

Up-conversion luminescence and temperature sensing properties of Ho3+/Gd3+ co-doped YbNbO4 phosphors

Up-conversion Luminescence and Thermal Sensing Properties of LuYO3: Er3+/Yb3+ Phosphor

Effects of Er3+ and Yb3+ Concentrations on Upconversion Luminescence and Thermal Sensing Characteristics of Sc2O3:Er3+/Yb3+ Phosphors

Sensitive Ho3+,Yb3+ co-doped mixed sesquioxide single crystal fibers thermometry based on upconversion luminescence

Effect of Lu3+ doping on photoluminescence characteristics of Y2.691Gd0.3Al5O12:0.3at%Ce phosphor ceramics

On fast LuAG:Ce scintillation ceramics with Ca 2+ co‐dopants

Fabrication and Optical Properties of Ce, Pr Co-doped LuAG Transparent Ceramics

Dense Ce3+ doped Lu3A15O12 ceramic scintillators with low sintering adds: Doping content effect, luminescence characterization and proton irradiation hardness

The effect of Lu3+ doping upon YAG:Ce phosphor ceramics for high-power white LEDs