Micromechanical modeling, thermal, and dielectric studies of poly (methyl methacrylate)-barium titanate composites

K. Umashankar G. Kamala Vasanth R. Krishna Prasad Department of Chemical Engineering and Materials Science,Centre of Excellence in Advanced Materials and Green Technologies,Amrita School of Engineering,Amrita Vishwa Vidyapeetham,Coimbatore,India

DOI: https://doi.org/10.1080/1023666x.2024.2391802

2024-08-23

International Journal of Polymer Analysis and Characterization

Abstract:Polymer composites containing poly (methyl methacrylate) (PMMA) and barium titanate (BaTiO 3 ) were synthesized using the solution mixing method. The electrical conductivity of PMMA is 6 × 10 −9 S/cm, and adding 2% fillers reduces to 5 × 10 −9 S/cm. The melting point of PMMA is 373 °C, and adding 2% and 4% fillers increased it to 376 °C and 379 °C, respectively. The polymer chains become less mobile and block macromolecules on the filler surface. The modulus of elasticity and mechanical tensile stress of the polymer composites with a 5-wt% of BaTiO 3 are 759.3 MPa and 75.6 MPa, respectively. The breakdown strength of PMMA is 203 KV and reduces with the addition of 5% filler to 144 KV. The values of E c / E m evaluated using the Tsai-Pagano, Christensen-Waals, ROM, Mori-Tanaka, and Halpin-Tsai models underpredict the modulus compared to experimental E c / E m values. Fourier spectroscopy confirmed the presence of Ti-O and BaTiO 3 bonds in the polymer composite. Scanning electron microscope images reveal spherical aggregates of BaTiO 3 coated with PMMA and an interparticle network. The dielectric constant of PMMA is 3 and increased with the addition of 2% and 4% fillers to 4 and 4.3, respectively.

polymer science