Abstract:SiMo ductile cast iron combines ease of part fabrication with good mechanical properties, including a usable plasticity range. Its poor corrosion resistance inherited from grey cast iron could be alleviated through alloying with Al or Cr additions capable of forming a dense oxide scale protecting the substrate. However, the presence of Al and Cr in cast iron tends to make the material brittle, and their optimum alloying additions need to be studied further. The present work was aimed at investigating the effect of crystallization rates on microstructure changes during directional crystallization of SiMo-type alloys with up to 3.5% Al and 2.4% Cr. The experiment was performed using the Bridgman–Stockbarger method. The tubular crucible was transferred from the hot section to cold section at rates ranging from 5 mm/h to 30 mm/h with a 4/5 crucible length and then quenched. The introduced Al promoted graphitization up to a point, wherein, at the highest applied addition, the graphite precipitation preceded crystallization of the rest of the melt. A rising level of Cr in these alloys from 1% to 2.4% resulted in the formation of low and high contents of pearlite, respectively. The higher crystallization rates proved effective in increasing the ferrite content at the expense of pearlite. In the investigated cast iron samples with smaller applied alloying additions, Widmanstätten ferrite or ausferrite, i.e., fine acircular phase, were often found. The switch from directional crystallization to quenching caused a transition from a liquid to solid state, which started with nucleation of islands of fine austenite dendrites with chunky graphite eutectic separating them. As these islands expanded, they pushed alloying additions to their sides, promoting carbide or pearlite formation in these places and forming a super-cell-like structure. The performed experiments helped gather information concerning the sensitivity of the microstructure of SiMo cast iron modified with Al and Cr to crystallization rates prevailing in heavy cast structures.

Effects of Silicon in High-Cr White Cast Irons

Effect of Si on Microstructure and Wear Resistance of Hypereutectic High-Chromium Cast Iron

Effect of Silicon on Precipitates of High-Silicon Austenitic Stainless Steel

The Effect of the Substitution of Silicon by Aluminum on the Properties of Lamellar Graphite Iron

Experimental Simulation of Directional Crystallization of SiMo Cast Iron Alloyed with Al and Cr

Characterization of Microstructure and Mechanical Properties of High Chromium Cast Irons Using Sem and Nanoindentation

Effect of quenching temperature on microstructure and properties of low silicon hypereutectic high chromium cast iron

Carbides in High-Speed Steels Containing Silicon

Effect of Chromium Content on Heat Treatment Behavior of Multi-Alloyed White Cast Iron for Abrasive Wear Resistance

Effect of Chromium on Microstructure and Properties of High Boron White Cast Iron

Effect of total iron and silicon contents and homogenization on the microstructure and performance of 6201 Al–Mg–Si ingots

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

The effect mechanism of Si on the cementite growth behavior in Fe–Cr–C steel: first-principles calculations and experiments

Effect of tempering temperature on microstructure and properties of low silicon hypereutectic high chromium cast ironAuswirkung der Anlasstemperatur auf das Gefüge und die Eigenschaften von übereutektischem Gusseisen mit niedrigem Siliziumgehalt und hohem Chromgehalt

The Effect of Silicon Addition on the High Temperature Oxidation of a Fe-Cr Alloy

Effect of quenching temperature on microstructure and properties of multivariate high chromium cast iron

Effect of Cu addition on hardness and microstructural features of low alloy white cast iron

Effect of Silicon on Thermal Stability of 4Cr3Mo2V Hot-Work Die Steel

Effect of Carbon and Cooling Rate on the Structure of Hypereutectic High Chromium Cast Iron in the Cast State and after Heat Treatment

Microstructure and Mechanical Properties of High Boron White Cast Iron with about 4 Wt% Chromium

Investigation of phase transformation and mechanical properties of silicon addition on AlCrFeMnNi high entropy alloys