Abstract:Abstract Microstructural evolution occurs in lead free Sn-Ag-Cu (SAC) solder joints exposed to isothermal aging. Such changes lead to degradations in the mechanical properties and creep behavior of the solder, and can result in dramatic reductions in the board level reliability of lead-free electronic assemblies subjected to aging. In our recent research, Scanning Electron Microscopy (SEM) has been used to: (1) monitor aging induced microstructural changes occurring within fixed regions in selected lead-free solder joints, (2) create time-lapse imagery of the microstructure evolution, and (3) analyze the microstructural changes quantitatively and correlate to the observed mechanical behavior evolution. This approach has removed the limitations of many prior studies where aged and non-aged microstructures were taken from two different samples and could only be qualitatively compared. In our current study, the microstructural evolutions were observed in SAC305 (96.5Sn-3.0Ag-0.5Cu) and SAC_Q (SAC+Bi) exposed to isothermal conditions at T = 100 °C and 125 °C for several different regions from several different joints. The microstructures in several fixed regions of interest were recorded after predetermined time intervals of aging, which were 1 hour (up to 270 hours) and 250 hours (up to 7000 hours) for the long-term aging samples. The aging induced changes in microstructure have been correlated with the changes in mechanical behavior measured using uniaxial tensile testing. The area and diameter of each IMC particle were tracked during the aging process using the recorded images and imaging processing software. As expected, the analysis of the evolving SAC305 and SAC+X microstructures showed a significant amount of diffusion of silver and bismuth in the beta-tin matrix during aging. In particular, Ag3Sn particles coalesced during aging leading to a decrease in the number of particles. Any bismuth in the SAC+X microstructure was observed to quickly go into solution, resulting in solid solution strengthening. This primary occurred within the beta-Sn dendrites, but also in the Ag3Sn intermetallic rich regions between dendrites. The presence of bismuth in was also found to slow the diffusion process that coarsens the Ag3Sn IMC particles. The combination solid solution strengthening and a lower diffusion rate for Ag lead to reduced aging effects in the SAC+Bi alloy relative to the SAC305 solder alloy. The SAC_Q alloy was found to have significantly better high temperature mechanical properties relative to SAC305 at all prior aging conditions. In particular, the initial modulus and ultimate tensile strength of SAC305 experienced large degradations during high temperature aging, whereas the same properties of SAC_Q changed only slightly. These changes in mechanical behavior correlated well with the observed increases in the average IMC particle diameter and decreases in the number of IMC particles. The microstructural and material property degradations were especially large for SAC305 during the initial 50 hours of aging.

Micromechanical and microstructure evolution of leaded (SnPb) and lead-free (SAC305 and SnCu) mixed solder joints during isothermal aging

Microstructure and Shear Strength of Sn37Pb/Cu Solder Joints Subjected to Isothermal Aging

Investigation and Comparison of Aging Effects in SAC305 and Doped SAC+X Solders Exposed to Isothermal Aging

Microstructure evolution and mechanical properties of Sn-9Zn-2.5Bi-1.5In solder joints with aging treatment under various conditions

Effects of aging time and temperature on shear properties of Sn–Zn and Sn–Ag–Cu solder joints

Effect of Nano-Cu 6 Sn 5 upon development mechanism of Cu–Ni–Sn compounds and mechanical characteristics for mixed solder joints

Interface evolution and mechanical properties of Sn–36Pb–2Ag solder joints under different aging conditions

Microstructure Evolution Of Solder Joints With Different Pb Contents At Ultra-Low Temperature

Study on the Microstructure Evolution and Mechanical Properties of Cu/Cu41Sn11/Cu Solder Joint During High-Temperature Aging

Grain orientations and failures mechanism of isothermal aged nano Sn-3Ag-0.5Cu/Cu solder joints by microwave hybrid heating and sheer mechanical strength

Reliability study of industry Sn3.0Ag0.5Cu/Cu lead-free soldered joints in electronic packaging

Microstructure evolution and growth kinetics of intermetallic compound in SAC305/Ag and SAC305/Cu solder joints during solid-state aging

Effect of Thermal Aging on the Interfacial Reaction Behavior and Failure Mechanism of Ni-xCu/Sn Soldering Joints under Shear Loading

Tensile Properties of Cu/Sn–58Bi/Cu Soldered Joints Subjected to Isothermal Aging

Microstructure and mechanical behavior of Sn15Bi-xAg\Cu solder joints during isothermal aging

In-situ fusion process and Cu–Sn compounds evolution mechanism of nano-intermetallic compound mixed solder joints

Reliability Risk Mitigation in Advanced Packages by Aging-Induced Precipitation of Bi in Water-Quenched Sn-Ag-Cu-Bi Solder

Mechanical Response of Cu/Sn58Bi-xNi/Cu Micro Solder Joint with High Temperatures

Microstructural Evolution and Mechanical Reliability of Transient Liquid Phase Sintered Joint During Thermal Aging

Stereological Analysis of Microstructural Evolution Due to Aging in SnAgCu Solder Alloys

In-situ isothermal aging TEM analysis of a micro Cu/ENIG/Sn solder joint for flexible interconnects