Simulated effects of main properties and heat flux on first dripping behaviors of polymers impinged by small flames

Yong Wang,Lei Duan,Aohui Zhou,Hongyan Yao,Ying Lu

DOI: https://doi.org/10.1016/j.firesaf.2024.104115

IF: 3.78

2024-02-12

Fire Safety Journal

Abstract:Dripping plays a significant role in understanding the UL-94 vertical test. In this study, the dripping of polymers impinged by small flames was simulated using the volume of fluid method and the enthalpy-porosity technique. The UL-94 flame was approximated using a 2026K gas flow with a velocity of 0.9 m/s, meeting with ASTM-D5207. The small-size drop and the large-size drop were characterized by aspect ratios of no more than 1.1 and greater than 3.1, respectively. Decreasing surface tension ( σ ), viscosity ( μ ), thermal conductivity ( k ), or increasing the heat flux tends to result in small-size drops. When σ ≤ 0.04 N/m, the first drop is small-size, and the equivalent radius of the first drop follows a power-law relationship with σ . As σ varies from 0.03 N/m to 0.07 N/m, the critical value of μ decreases from 0.30 Pa·s to 0.02 Pa s. If σ = 0.07N/m and k ≤ 0.1W/m·K, the first drop tends to be small-size. When σ is 0.03 N/m, the size of the first drop is independent of k , and the critical heat flux is approximately 48 kW/m 2 . The first dripping time increases with μ , and the large-size dripping time is linear with the product of viscosity and characteristic length divided by drop mass.

materials science, multidisciplinary,engineering, civil