Novel Bamboo-Mediated Biosynthesis of MnO x for Efficient Low-Temperature Propane Oxidation

Daifeng Lin,Xiaoshan Feng,Changlin Cao,Hun Xue,Yongjin Luo,Qingrong Qian,Lingxing Zeng,Baoquan Huang,Songwei Yang,Qinghua Chen

DOI: https://doi.org/10.1021/acssuschemeng.0c04412

2020-07-08

Abstract:Small-size MnO<i>_x</i> nanoparticles with good reducibility, fast lattice oxygen mobility, and large acid sites are first obtained by bamboo-mediated biosynthesis, showing promising propane (C₃H₈) oxidation activity. The COO–, −C–O–, and −C═O functional groups in bamboo powder (BP) act as complexing species, and the presence of organic carbon is responsible for bioreduction of Mn ions during calcination. The above bifunctional roles increase the content of Mn²⁺ in MnO<i>_x</i>, which contributes to large amounts of oxygen vacancies and then increases oxygen mobility, and the chief Mn substance of Mn³⁺ species in the obtained primary phase of Mn₂O₃ is recognized as the active sites for total C₃H₈ oxidation. It is revealed that BP treated by sequential NaOH (pH = 13) and HCl solutions (pH = 1) (BP-13-1) is the best media for biosynthesis, where alkaline treatment is to increase the number of complexing species and the acid solution is to eliminate the negative role of alkali metal ions (Na⁺, K⁺). As a result, the obtained BP-13-1-mediated biosynthesis of MnO<i>_x</i> (MnO<i>_x</i>-BP-13-1) shows a much higher reaction rate of 2.96 μmol_{C_3H8} g_cat^–1 s^–1 at 300 °C, while it is only 0.38 μmol _C₃H₈ g_cat^–1 s^–1 for the reference sample MnO<i>_x</i> without BP modification. Moreover, MnO<i>_x</i>-BP-13-1 shows excellent thermal stability and good resistance against 5 vol % H₂O and 5 vol % CO₂. Additionally, in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) results reveal that CH₂CHCH₃ is the dominant intermediate species in MnO<i>_x</i>-BP-13-1 with a lower reaction barrier compared to unmodified MnO<i>_x</i>.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c04412?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c04412</a>.Catalytic evaluation for C₃H₈ oxidation; physicochemical characterization; and (A) XRD patterns and (B) FT-IR spectra of (1) BP; (2) BP-13-1; (3) MnNO₃-BP; (4) MnNO₃-BP-13-1 (Figure S1); SEM images of (a) BP; (b) MnNO₃-BP;(c) BP-1; (d) MnNO₃-BP-1; (e) BP-7; (f) MnNO₃-BP-7; (g) BP-13; (h) MnNO₃-BP-13; (i) BP-1-13; (j) MnNO₃-BP-1-13; (k) BP-13-1; (l) MnNO₃-BP-13-1 (Figure S2); SEM-EDS results of (a, b) MnO<i>_x</i>-BP-13 and MnO<i>_x</i>-BP-1-13 (Figure S3); TEM image of (A) MnO<i>_x</i>-BP-13, HRTEM images of (B) MnO<i>_x</i>-BP-13 cuboid and (C) MnO<i>_x</i>-BP-13 nanoparticles (Figure S4); the ash content in the untreated and treated BP (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c04412/suppl_file/sc0c04412_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology