Abstract:Compared with the crystalline transition metal oxyhydroxide, low-crystalline structure is conducive to high electrochemical performance due to its more grain boundaries and ion diffusion channels. However, the manufacture of low-crystalline oxyhydroxides remains challenging, especially those with multiple transition metals. Herein, high mass loading (∼9 mg cm−2) and low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth (CC) were prepared by electrochemical reconstruction. The low-crystalline Ni/Co-oxyhydroxides nanoarrays possessed a hierarchical structure, which were consist of flake-like (Co0.25, Ni0.75)O(OH) single-crystals and needle-like Ni-doped CoO(OH) polycrystalline. Both single crystal nanoflakes and polycrystalline nanoneedles contained a lot of defects. Owing to the unique structure, the mutual doping of Ni and Co atoms, and the abundant defects, the nanoarrays of Ni/Co-3500 showed excellent electrochemical performance with a high specific capacitance of 8.87 F cm−2 at 5 mA cm−2 and a high rate retention of 69.33% at 50 mA cm−2, as well as a high cycle stability remaining 91.6% of initial capacitance after 2000 galvanostatic charge-discharge cycles at a current density of 20 mA cm−2. Furthermore, the assembled asymmetric supercapacitor of Ni/Co-3500//oxidized CC delivered a high areal capacitance of 1.48 F cm−2 and a volumetric capacitance of 14.8 F cm−3 at 8 mA cm−2, as well as 1.11 F cm−2 (11.1 F cm−3) even at 50 mA cm−2. The energy density of Ni/Co-3500//oxidized CC device was up to 4.35 mWh cm−3 at the powder density of 60.1 mW cm−3. It indicates that the as-prepared low-crystalline Ni/Co-oxyhydroxides arrays on CC is a promising electrode for high energy density supercapacitors.

Cattail spike-like Co(OH)F@Co3O4 nanoarrays for high-performance supercapacitors

Co3O4@CoNi-LDH Core/shell Nanosheet Arrays for High-Performance Battery-Type Supercapacitors

NiCo2S4@Ni3S2 Hybrid Nanoarray on Ni Foam for High-Performance Supercapacitors

Design of a porous cobalt sulfide nanosheet array on Ni foam from zeolitic imidazolate frameworks as an advanced electrode for supercapacitors.

Co3S4 Nanoplate Arrays Decorated with Oxygen-Deficient CeO2 Nanoparticles for Supercapacitor Applications

Co(OH)F@CoP/CC core-shell nanoarrays for high-performance supercapacitors

Facilely synthesized porous NiCo2O4 flowerlike nanostructure for high-rate supercapacitors

The hetero-structured nanoarray construction of Co3O4 nanowires anchored on nanoflakes as a high-performance electrode for supercapacitors

Advanced binder-free electrodes based on CoMn2O4@Co3O4 core/shell nanostructures for high-performance supercapacitors

CoO@CoS/Ni3S2 hierarchical nanostructure arrays for high performance asymmetric supercapacitor

Highly stable Co3O4 nanoparticles/carbon nanosheets array derived from flake-like ZIF-67 as an advanced electrode for supercapacacitor

Thin Co 3 O 4 Nanosheet Array on 3D Porous Graphene/nickel Foam As a Binder-Free Electrode for High-Performance Supercapacitors

3D net-like Co3O4@NiO nanostructures for high performance supercapacitors

Hierarchical three-dimensional nanoflower-like CuCo2O4@CuCo2S4@Co(OH)2 core-shell composites as supercapacitor electrode materials with ultrahigh specific capacitances

Porous chopsticks-like FeCo2O4 by the hydrothermal method for high-performance asymmetric supercapacitors

Low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth with high mass loading and hierarchical structure as cathode for supercapacitors

In-situ Fabrication of Co Foam@co3o4 Porous Nanosheet Arrays for High Performance Supercapacitors

Hierarchical NiCo2O4@NiCo2O4 Core/shell Nanoflake Arrays As High-Performance Supercapacitor Materials.

Core-shell nanostructured MnO2@Co9S8 arrays for high-performance supercapacitors

Self-assembly of hierarchical 3D starfish-like Co3O4 nanowire bundles on nickel foam for high-performance supercapacitor

Ethanol-assisted Solvothermal Synthesis of Porous Nanostructured Cobalt Oxides (coo/co3o4) for High-Performance Supercapacitors