Low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth with high mass loading and hierarchical structure as cathode for supercapacitors

Menghua Pan,Weiliang Zeng,Hongying Quan,Jingmiao Cui,Yao Guo,Yunying Wang,Dezhi Chen

DOI: https://doi.org/10.1016/j.electacta.2020.136886

IF: 6.6

2020-10-01

Electrochimica Acta

Abstract:<p>Compared with the crystalline transition metal oxyhydroxide, low-crystalline structure is conducive to high electrochemical performance due to its more grain boundaries and ion diffusion channels. However, the manufacture of low-crystalline oxyhydroxides remains challenging, especially those with multiple transition metals. Herein, high mass loading (∼9 mg cm⁻²) and low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth (CC) were prepared by electrochemical reconstruction. The low-crystalline Ni/Co-oxyhydroxides nanoarrays possessed a hierarchical structure, which were consist of flake-like (Co_0.25, Ni_0.75)O(OH) single-crystals and needle-like Ni-doped CoO(OH) polycrystalline. Both single crystal nanoflakes and polycrystalline nanoneedles contained a lot of defects. Owing to the unique structure, the mutual doping of Ni and Co atoms, and the abundant defects, the nanoarrays of Ni/Co-3500 showed excellent electrochemical performance with a high specific capacitance of 8.87 F cm⁻² at 5 mA cm⁻² and a high rate retention of 69.33% at 50 mA cm⁻²<strong>,</strong> as well as a high cycle stability remaining 91.6% of initial capacitance after 2000 galvanostatic charge-discharge cycles at a current density of 20 mA cm⁻². Furthermore, the assembled asymmetric supercapacitor of Ni/Co-3500//oxidized CC delivered a high areal capacitance of 1.48 F cm⁻² and a volumetric capacitance of 14.8 F cm⁻³ at 8 mA cm⁻², as well as 1.11 F cm⁻² (11.1 F cm⁻³) even at 50 mA cm⁻². The energy density of Ni/Co-3500//oxidized CC device was up to 4.35 mWh cm⁻³ at the powder density of 60.1 mW cm⁻³. It indicates that the as-prepared low-crystalline Ni/Co-oxyhydroxides arrays on CC is a promising electrode for high energy density supercapacitors.</p>

electrochemistry