Abstract:Compared with the crystalline transition metal oxyhydroxide, low-crystalline structure is conducive to high electrochemical performance due to its more grain boundaries and ion diffusion channels. However, the manufacture of low-crystalline oxyhydroxides remains challenging, especially those with multiple transition metals. Herein, high mass loading (∼9 mg cm−2) and low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth (CC) were prepared by electrochemical reconstruction. The low-crystalline Ni/Co-oxyhydroxides nanoarrays possessed a hierarchical structure, which were consist of flake-like (Co0.25, Ni0.75)O(OH) single-crystals and needle-like Ni-doped CoO(OH) polycrystalline. Both single crystal nanoflakes and polycrystalline nanoneedles contained a lot of defects. Owing to the unique structure, the mutual doping of Ni and Co atoms, and the abundant defects, the nanoarrays of Ni/Co-3500 showed excellent electrochemical performance with a high specific capacitance of 8.87 F cm−2 at 5 mA cm−2 and a high rate retention of 69.33% at 50 mA cm−2, as well as a high cycle stability remaining 91.6% of initial capacitance after 2000 galvanostatic charge-discharge cycles at a current density of 20 mA cm−2. Furthermore, the assembled asymmetric supercapacitor of Ni/Co-3500//oxidized CC delivered a high areal capacitance of 1.48 F cm−2 and a volumetric capacitance of 14.8 F cm−3 at 8 mA cm−2, as well as 1.11 F cm−2 (11.1 F cm−3) even at 50 mA cm−2. The energy density of Ni/Co-3500//oxidized CC device was up to 4.35 mWh cm−3 at the powder density of 60.1 mW cm−3. It indicates that the as-prepared low-crystalline Ni/Co-oxyhydroxides arrays on CC is a promising electrode for high energy density supercapacitors.

In-situ fabricated porous Ni-Co-Mo based nanosheet array electrodes for hybrid supercapacitors with long-cycle stability

NiCo2S4@Ni3S2 Hybrid Nanoarray on Ni Foam for High-Performance Supercapacitors

Design of a porous cobalt sulfide nanosheet array on Ni foam from zeolitic imidazolate frameworks as an advanced electrode for supercapacitors.

A Zinc Cobalt Sulfide Nanosheet Array Derived from a 2D Bimetallic Metal-Organic Frameworks for High-Performance Supercapacitors

A Few Atoms Thick Nickel–Cobalt Oxides Mesoporous Nanosheets and Their Arrays on Ni Foam for Supercapacitors with Ultra-Long Cycling Lifespan

Manganese Doped Co3O4 Mesoporous Nanoneedle Array for Long Cycle-Stable Supercapacitors

In Situ Growth of Nico2s4 Nanotube Arrays on Ni Foam for Supercapacitors: Maximizing Utilization Efficiency at High Mass Loading to Achieve Ultrahigh Areal Pseudocapacitance

Synthesis of NiMn-LDH Nanosheet@Ni 3 S 2 Nanorod Hybrid Structures for Supercapacitor Electrode Materials with Ultrahigh Specific Capacitance

Three-Dimensional Hierarchical Structure ZnO@C@NiO on Carbon Cloth for Asymmetric Supercapacitor with Enhanced Cycle Stability

Nanohybridization of Ni–Co–S Nanosheets with ZnCo 2 O 4 Nanowires as Supercapacitor Electrodes with Long Cycling Stabilities

Battery-type ZnCo 2 O 4 nanosheets and nanowires as advanced cathode materials for hybrid supercapacitors with ultra-long cycling stability

NiCo2O4 nanosheet stereostructure with N-doped carbon/Co array supports derived from Co-MOF for asymmetric supercapacitor

A dual CoNi MOF nanosheet/nanotube assembled on carbon cloth for high performance hybrid supercapacitors

MOFs assisted construction of Ni@NiOx/C nanosheets with tunable porous structure for high performance supercapacitors

In situ grown NiFeP@NiCo<sub>2</sub>S<sub>4</sub> nanosheet arrays on carbon cloth for asymmetric supercapacitors

In situ growth of NiCo2O4 nanosheets arrays on Ni foam for high-performance supercapacitor

MOF-derived NiZnCo-P nano-array for asymmetric supercapacitor

Low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth with high mass loading and hierarchical structure as cathode for supercapacitors

Nickel–Cobalt-Layered Double Hydroxide Nanosheets Supported on NiMoO 4 Nanorods with Enhanced Stability for Asymmetric Supercapacitors

Porous NiCo2O4–FeCo2O4 Nanowire Arrays As Advanced Electrodes for High-Performance Flexible Asymmetric Supercapacitors

NiCo 2 S 4 nanosheets decorated on nitrogen-doped hollow carbon nanospheres as advanced electrodes for high-performance asymmetric supercapacitors