Abstract:In this work, a novel dendritic copolymer PNSi-co-MP as an intumescent flame retardant was fabricated using a silicon-, phosphorus- and nitrogen-containing monomer (PNSi) and melamine phosphate (MP). Random copolymerization way disrupted the regularity of monomer arrangement, resulting in the thermal deformation behavior of PNSi-co-MP being different from the self-polymerized macromolecule (MPNSi) / melamine polyphosphate (MPP) system. Consequently, PNSi-co-MP was distributed reasonably evenly in the polypropylene (PP) matrix, and some of the PNSi-co-MP particles deformed to 200–300 nm from 5 to 10 μm. More importantly, the toughness of PNSi-co-MP/PP was dramatically increased compared with MPNSi/MPP/PP. Specifically, 16PNSi-co-4MP/PP exhibited a 278% higher elongation at break and a 33.3% higher unnotched impact strength compared to 16MPNSi/4MPP/PP. Furthermore, PNSi-co-MP exhibited a rapid charring effect in PP. In a cone calorimeter test, the maximum combustion intensity of the composite was inhibited in only 17 s by the PNSi-co-MP molecule. Compared with the pure PP, the composite with 20 wt% 12PNSi-co-8MP showed a 93.6% lower peak heat release rate and an 87.2% lower smoke production rate, indicating its excellent flame retardancy. The composites containing copolymer molecules also performed much higher flame retardancy than MPNSi/MPP/PP sample, although their chemical composition was almost the same except for the linking form of flame-retardant monomers. PNSi-co-MP simultaneously endowed PP with a higher limited oxygen index, glow wire flammability index, glow wire ignition temperature, residue yield, and fire safety performance than MPNSi/MPP. The reason for this was that the copolymerization strategy aggregated the flame-retardant monomers into one molecule, thus effectively promoting the charring reaction. Accordingly, this work provided a new method for preparing flame-retardant molecules with comprehensive performance through molecular composition and structural design.

Flame retardancy in isotactic polypropylene modified with crystalline coordination polymers based on calcium, zinc or aluminum dimethyl phosphates

Flame Retardation and Thermal Degradation of Intumescent Flame‐retarded Polypropylene Composites Containing Spirophosphoryldicyandiamide and Ammonium Polyphosphate

A Novel Halogen‐free Intumescent Flame Retardant Containing Phosphorus and Nitrogen and Its Application in Polypropylene Systems

Improving the flame retardancy and mechanical properties of high-density polyethylene-g-maleic anhydride with a novel organic metal phosphonate

Synthesis of a Novel Intumescent Flame Retardant and Its Flame Retardancy in Polypropylene

Simultaneously Enhancing the Flame Retardancy, Water Resistance, and Mechanical Properties of Flame-Retardant Polypropylene via a Linear Vinyl Polysiloxane-Coated Ammonium Polyphosphate

Preparation of a Cobalt Metal-Organic Framework (Co-Mof) and Its Application As a Polypropylene Flame Retardant by Compounding with Melamine Polyphosphate

Synergistic effect between a char forming agent (CFA) and microencapsulated ammonium polyphosphate on the thermal and flame retardant properties of polypropylene

Flame-retardant Effects of NH2-MIL-53(Al) in Combination with Phosphorus-Containing and Nitrogen-Containing Flame Retardants on Polypropylene

Great enhancement of efficiency of intumescent flame retardants by titanate coupling agent and polysiloxane

From physical mixtures to block copolymer: Impose outstandingly toughening and flame retardant effect to polypropylene

Dendritic copolymers from P-, N- and Si-based monomer and melamine phosphate generate thermal deformation toughening and a rapid charring flame retardant effect in polypropylene

Flame-retardant and thermal properties of highly efficient water-resistant intumescent flame-retardant polypropylene composites

Highly efficient replacement of traditional intumescent flame retardants in polypropylene by manganese ions doped melamine phytate nanosheets

Synergistic effect of expandable graphite and intumescent flame retardants on the flame retardancy and thermal stability of polypropylene

Effect of phytic acid-modified layered double hydroxide on flammability and mechanical properties of intumescent flame retardant polypropylene system

Study on Flame Retardance of Co‐microencapsulated Ammonium Polyphosphate and Dipentaerythritol in Polypropylene

Hyperbranched Phosphorus/nitrogen-Containing Polymer in Combination with Ammonium Polyphosphate As a Novel Flame Retardant System for Polypropylene

Mode of Action of Zn-DOPOx and Melamine Polyphosphate as Flame Retardants in Glass Fiber-Reinforced Polyamide 66

Microencapsulated Ammonium Polyphosphate with Polyurethane Shell: Application to Flame Retarded Polypropylene/Ethylene-Propylene Diene Terpolymer Blends

Synthesis of a hyperbranched phosphorus-containing polyurethane as char forming agent combined with ammonium polyphosphate for reducing fire hazard of polypropylene