Abstract:Nearly monodispersed CaWO4 hollow microspheres with controlled diameters were successfully prepared by a facile one-step hydrothermal method using CaCl2, Na2WO4, and sodium dodecyl sulfate (SDS) as the starting reaction reagents and distilled water as solvent. The crystal structure, morphology, macroporous and photoluminescence properties of the as-synthesized products are characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, selected-area electron diffraction, nitrogen adsorption-desorption isotherm technique, and fluorescence spectrometer. The hollow microspheres have an average diameter of 2.2 mu m and hollow interior of 0.5-1 mu m. The shell is consisting of numerous nanoparticles 45 nm in diameter. The effects of SDS amount, pH value, concentrations of reaction reagents, and reaction durations have been studied systematically. The results indicate that a certain SDS amount plays a key important role in the final formation of hollow microspheres. It is also found that the average diameters of the hollow spheres can also be tuned by increasing the SDS amount in the range of 0.2-1 g into the reaction system. Based on the detailed investigation on the influences of experimental parameters, the formation mechanism of the hollow interiors by a SDS-induced Ostwald ripening process is proposed for the CaWO4 hollow microspheres. The B runauer-Emmett-Teller (BET) surface areas and pore volume of the CaWO4 hollow microspheres are 14.4 m(2)/g and 0.087 cm(3)/g, respectively. Furthermore, photoluminescence spectrum of the CaWO4 hollow microspheres reveals a strong and broadband from 350 to 450 nm with an emission peak at 413 nm originating from the WO42- groups. This Ostwald ripening process could open novel and efficient pathway for the preparation of ternary metal oxides with hollow interiors.

Microfluidic synthesis of calcium tungstate CaWO4

Microfluidic Vaterite Synthesis: Approaching the Nanoscale Particles

The synthesis and photoluminescent properties of calcium tungstate nanocrystals

Shape-controlled of CaWO4 microcrystals by self-assembly of nanocrystals via a simple sonochemical method

Nearly Monodisperse Tungstate MWO4 Microspheres (M = Pb, Ca): Surfactant-Assisted Solution Synthesis and Optical Properties

Mono-Disperse CaWO4 Microsphere with Hierarchical Structures: Room Temperature Synthesis and Its Optical Properties

Synthesis and Characterization of Nano-Calcium Tungstate Thin Film Via Chemical Solution Processing

An approach for synthesizing various types of tungsten oxide nanostructure.

Microwave-assisted synthesis and characterization of luminescent lead tungstate microcrystals

Hydrothermal Synthesis of Tungsten Oxide Micro/Nanostructures

Solvothermal Synthesis and Characterization of Crystalline CaWO4 Nanoparticles

Novel synthesis of hierarchical tungsten carbide micro-/nanocrystals from a single-source precursor

Synthesis of Nanostructured Tungsten Oxide Thin Films: A Simple, Controllable, Inexpensive, Aqueous Sol−Gel Method

Controllable Synthesis of Hierarchical Nanostructures of Cawo4 and Srwo4 Via A Facile Low-Temperature Route

Controlled Synthesis of Calcium Tungstate Hollow Microspheres via Ostwald Ripening and Their Photoluminescence Property

Laminar flow synthesis of submicron CaCO$_3$ particles in 3D printed microfluidic chips

Large-Scale Synthesis of Tungsten Single-Crystal Microtubes Via Vapor-Deposition Process

Synthesis of CaWO4 Nanoparticles by a Molten Salt Method

Microfluidic Synthesis of ZnWO4 Nanoparticles and Its Performance in DMSO-containing Wastewater Treatment

Synthesis of Coarse-Grained Tungsten Carbide Directly from Scheelite/Wolframite by Carbothermal Reduction and Crystallization

Continuous-Flow Synthesis of Perovskite Particles for Optical Application