Abstract:The effects of temperature on the tribological and dynamic mechanical properties (DMP) of aromatic liquid-crystal poly(ester-co-amide) were investigated. Specimens for the DMA test and friction and wear test were prepared by compression molding at elevated temperature. The dynamic mechanical properties of the resulting compression-molded liquid crystal polymer (LCP) specimens were evaluated on a Perkin-Elmer DMA instrument, in a three-point bending mode, at a heating rate of 10°C/min and frequency of 1Hz from room temperature to 250°C. The friction and wear behavior of the compression-molded LCP specimens sliding against SA52100 steel in a ball-on-disk configuration was evaluated on a high-temperature friction and wear tester from 25 to 300°C. The worn surface morphologies of the compression-molded LCP specimens were observed on a scanning electron microscope. It was found that the tribological and dynamic mechanical properties of the LCP strongly depended on the test temperature. Namely, the friction coefficients decreased significantly and the wear rate increased considerably with increasing temperature. This was attributed to the enhanced softening and plastic deformation of the LCP at elevated temperature. The LCP experienced severe plastic deformation, flowing and local melting owing to the destruction of the stiff backbones of the polymeric molecules at excessively high temperature, thus the largest wear rate of the tested LCP was generated at 300°C. Such a trend in the friction and wear behavior of the compression-molded LCP with temperature conformed well to the corresponding worn surface morphologies. Namely, the LCP worn surface was characterized by mild plastic deformation and micro-cracking as the LCP disk slid against the steel ball at 50°C, whilst at 100°C, the plastic deformation and adhesion became severe and the micro-cracking disappeared owing to the plastic flow. The plastic deformation and adhesion became increasingly more severe with further increase of the test temperature up to 150, 200, and 250°C, owing to the increased plastic flow and local softening and melting of the LCP. Moreover, the storage modulus of the compression-molded LCP greatly decreased with increasing temperature, as did the loss modulus, while the complex modulus and tan δ increased with increasing temperature, which agreed well with the corresponding trend of the tribological behavior with temperature. It was confirmed that the dynamic mechanical properties of the polymer were an important factor of the high temperature tribological behavior.

Polymer transfer film formation from cryogenic to elevated temperatures

Tribology of self-lubricating high performance ATSP, PI, and PEEK-based polymer composites up to 300 °C

Effect of Temperature on the Tribological and Dynamic Mechanical Properties of Liquid Crystalline Polymer

Role of transfer film formation on the tribological properties of polymeric composite materials and spherical plain bearing at low temperatures

Abrasive wear of PEEK and ATSP-based polymer composite coatings under lunar regolith conditions

Synergistic Enhancement of the High-Temperature Friction and Wear Behavior of PTFE Matrix Composites with the Addition of CF, PEEK, and TiC

Effect of Low-Friction Composite Polymer Coatings Fabricated by Electrophoretic Deposition and Heat Treatment on the Ti-6Al-4V Titanium Alloy’s Tribological Properties

Tribological Properties of PTFE-based Fabric Composites at Cryogenic Temperature

Construction of a PTFE-based lubricant film on the surface of Nomex/PTFE fabric to enhance the tribological performance at cryogenic temperatures

Tailoring Polyimide Composites with Low Friction and Wear at High Temperatures

Lubricating Performance of Polytetrafluoroethylene Hybrid Fabric Composites with Removed Thermosetting Resin at Cryogenic Temperatures

Tribological Behavior of Reinforced PTFE Composites and Un-Reinforced Polyketone-Based Materials against Coated Steel

In-situ observation of transfer film formation and evolution for the fabric composite lubricated spherical plain bearing at cryogenic and wide temperature range

Physical and Chemical Evolution of PTFE-α-Al2O3 Composites Versus 304 SS Tribofilms During Dry Sliding

The tribological properties of PTFE filled with thermally treated nano-attapulgite

Improving the tribological performance of CFRPTFE at elevated temperature by sliding against Ti-TiCx/DLC film

Effect of temperature on the tribological properties of Polytetrafluoroethylene/Kevlar fabric/phenolic composites

Friction and Wear Behavior of PTFE Coatings Modified with Poly (methyl Methacrylate)

Tribological properties of PTFE/Kevlar fabric composites under heavy loading

Research on the Effect of Temperature on Tribological Properties of PTFE Composites under Oil Lubrication Conditions

Multiscale insight to tribological mechanism of PTFE/aramid fiber composite liner containing PES/PMPS microcapsules under a high temperature environment