Pr3+-Er3+ co-doped Ba3.75Gd0.833Nb10O30 glass-ceramics for tunable luminescence, optical anti-counterfeiting and temperature sensing

Tong Wang,Chunhui Su,Hongbo Zhang,Wuyunga Bao,Qianwen Wang

DOI: https://doi.org/10.1016/j.ceramint.2023.11.234

IF: 5.532

2023-11-01

Ceramics International

Abstract:Pr3+-Er3+ co-activated glass-ceramics containing Ba3.75Gd0.833Nb10O30 crystalline phase were prepared as a multifunctional material. The optimum heat treatment condition was determined to be 750 °C/90 min, as this condition is most favorable for luminescence. As the Pr3+ concentration increases, the emissions of 3P0 and 1D2 energy levels show different trends, leading to a shift in luminescence from orange to yellow. With the introduction of Er3+, the co-doped sample achieves orange-yellow-green tunable luminescence. The 0.3%Pr3+-0.3%Er3+ co-doped sample exhibits alternating yellow-orange-green luminescence during continuous excitation in the range of 250–500 nm, which has potential applications in optical anti-counterfeiting. In the temperature interval of 298–458 K, the maximum temperature sensitivities based on the NTCLs of Pr3+ and Er3+ were 0.82 × 10−2 K−1 (Sa) and 1.40 % K−1 (Sr). Meanwhile, the thermal repeatability ratio is higher than 92.3 %, which proved that it is a potential temperature sensing material. In addition, the concentration quenching, energy transfer and luminescence phenomena involved were analyzed in depth and their mechanisms were explained.

materials science, ceramics