Abstract:Mg alloy has attracted researchers' attention as applied for novel biomedical material because of its super corrosion property and well biocompatibility. Ultra-fine grain (UFG) Mg alloy has certain advantages in the development of medical devices because of its good plasticity and corrosion resistance. Equal channel angular pressing (ECAP) was performed on Mg-3Sn-0.5Mn alloy successfully. The microstructure and grain size were observed and measured by OM and TEM. The mechanical property was tested by microhardness and tensile test, the texture oriented was experimented by XRD, and the corrosion property was tested by electrochemical experiment. After 4 passes ECAP at 320 degrees C, the average grain size of Mg-3Sn-0.5Mn alloy reached 1.65 mu m, and local grain size reached 0.8 mu m. The grain refinement was caused by severe plastic deformation and recrystallization. The elongation increased from 22.2% to 58.6%, the tensile strength decreased from 242.8 MPa to 195.6 MPa after 4 passes deformation. The mechanical tests showed an improvement in the elongation after 4 passes, which were about 3 times higher than in the as-extruded sample, whereas the tensile strength decreased slightly. The texture of Mg-3Sn-0.5Mn alloy changed obviously which contributed to the actuating of the slip system. This change of texture contributed to the improvement of fracture elongation and decrease of tensile strength. The mechanical property of Mg-3Sn-0.5Mn alloy after ECAP was affected by the texture orientation and grain strengthening.

Microstructure evolution and mechanical properties of Mg–Mn–RE alloy processed by equal channel angular pressing

Microstructure and Mechanical Properties of Ultrafine Grained Mg97Y2Zn1 Alloy Processed by Equal Channel Angular Pressing

Microstructure and Mechanical Properties of Mg96Y3Zn1 Alloy Processed by Equal Channel Angular Pressing

Precipitation behaviors and mechanical properties of a solution-treated Mg-Gd-Nd-Zn-Zr alloy during equal-channel angular pressing process

Mechanical Properties of Biomedical Ultrafine Grained Mg-3Sn-0.5Mn Alloy Processed by Equal-Channel Angular Pressing

Improvement of Strength and Ductility of Mg-Zn-Ca-Mn Alloy by Equal Channel Angular Pressing

Microstructure and Mechanical Properties of Mg–Zn–Ca Alloy Processed by Equal Channel Angular Pressing

Microstructure Evolution and Mechanical Behavior of Mg-10Gd-3Y-0.4Zr Alloy Processed by ECAP at High Temperature

Equal-Channel Angular Pressing of Magnesium Alloy Az91 and Its Effects on Microstructure and Mechanical Properties

Microstructure Evolution and Mechanical Properties of Mg-Gd-Y-Zn-Zr Alloy During Equal Channel Angular Pressing

Anisotropy investigation of an ECAP-processed Mg-Al-Ca-Mn alloy with synergistically enhanced mechanical properties and corrosion resistance

The Effect of Particles on Microstructure and Mechanical Behaviour of Mg-10Gd-3Y-0.4Zr Alloy Processed by ECAP

Microstructural evolution and mechanical properties of AZ31 Mg alloy fabricated by a novel bifurcation-equal channel angular pressing

Microstructural Evolution and Mechanical Properties of Mg95.5Y3Zn1.5 Alloy Processed by Extrusion and ECAP

Microstructural evolution of Al-Mg-Er-Zr alloy by equal channel angular extrusion at room temperature

Characterization of microstructure in high strength Mg 96Y 3Zn 1 alloy processed by extrusion and equal channel angular pressing

Microstructure and Tensile Properties of A Mg-Zn-Y-Zr Alloy Containing Quasicrystal Phase Processed by Equal Channel Angular Pressing

Microstructure and mechanical properties of the Mg98.5Zn0.5RE1 (RE=Gd and/or Y) alloys processed by equal channel angular pressing

Preparing Mg-6Al alloy with high mechanical properties and fine grains by equal channel angular extrusion

Microstructure Evolution and Mechanical Properties of AZ 31 Mg Alloy Processed by Equal Channel Angular Extrusion

Mechanical Properties and Microstructure of Al–Mg–Mn–Zr Alloy Processed by Equal Channel Angular Pressing at Elevated Temperature