The Effect of Solution Treatment Duration on the Microstructural and Mechanical Properties of a Cold-Deformed-by-Rolling Ti-Nb-Zr-Ta-Sn-Fe Alloy

Vasile Dănuț Cojocaru,Nicolae Șerban,Elisabeta Mirela Cojocaru,Nicoleta Zărnescu-Ivan,Bogdan Mihai Gălbinașu

DOI: https://doi.org/10.3390/ma17040864

IF: 3.4

2024-02-13

Materials

Abstract:The study presented in this paper is focused on the effect of varying the solution treatment duration on both the microstructural and mechanical properties of a cold-deformed by rolling Ti-30Nb-12Zr-5Ta-2Sn-1.25Fe (wt.%) alloy, referred to as TNZTSF. Cold-crucible induction using the levitation synthesis technique, conducted under an argon-controlled atmosphere, was employed to fabricate the TNZTSF alloy. After synthesis, the alloy underwent cold deformation by rolling, reaching a total deformation degree (total applied thickness reduction) of 60%. Subsequently, a solution treatment was conducted at 850 °C, with varying treatment durations ranging from 2 to 30 min in 2 min increments. X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques were utilized for the structural analysis, while the mechanical properties were assessed using both tensile and hardness testing. The findings indicate that (i) in both the cold-deformed-by-rolling and solution-treated states, the TNZTSF alloy exhibits a microstructure consisting of a single β-Ti phase; (ii) in the solution-treated state, the microstructure reveals a rise in the average grain size and a decline in the internal average microstrain as the duration of the solution treatment increases; and (iii) owing to the β-phase stability, a favorable mix of elevated strength and considerable ductility properties can be achieved.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper aims to study the effect of solution treatment time on the microstructure and mechanical properties of cold-rolled Ti-30Nb-12Zr-5Ta-2Sn-1.25Fe (abbreviated as TNZTSF) alloy, and to develop a microstructure with a good balance of elastic modulus and high strength through an appropriate thermomechanical processing route.

Specifically, the paper explores the following points:
1. **Research Object**: A β-Ti alloy containing titanium (Ti), niobium (Nb), zirconium (Zr), tantalum (Ta), tin (Sn), and iron (Fe).
2. **Experimental Method**: First, the alloy is subjected to a cold rolling process to achieve a 60% thickness reduction, followed by solution treatment at 850°C for different times (ranging from 2 minutes to 30 minutes, with increments of 2 minutes).
3. **Analytical Techniques**: The microstructure is analyzed using X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques, and its mechanical properties are evaluated through tensile testing and hardness testing.
4. **Research Objective**: To investigate the effect of different solution treatment times on the alloy's microstructure (such as grain size, internal microstrain, etc.) and mechanical properties (such as strength and plasticity), in order to find the optimal heat treatment conditions to optimize the alloy's overall performance.