Abstract:In response to the poor tribo-corrosion resistance of titanium alloys in marine engineering applications, CoCrFeNiZrx (x = 0, 0.1, 0.2, 0.3, 0.4) coatings were synthesized on Ti6Al4V substrates using laser cladding technology. The effects of Zr on phase formation, microstructure, micro-hardness, and wear resistance of CoCrFeNi coatings in diverse environments were examined. A robust metallurgical bond was established between the coating and the substrate. Through X-ray diffraction analysis and thermodynamic calculations, it was confirmed that the coating primarily consists of α-Ti and Ti2Ni phases. The introduction of Zr led to the formation of a new phase (Zr2Ni). Through scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS) analysis, it is observed that with the increase in Zr content, leading to a greater infiltration of Ti from the substrate into the coatings. The grain refinement strengthening and solid solution strengthening mechanisms enhanced the micro-hardness of the coatings, which was approximately 1.6 ~ 2.1 times higher than that of the Ti6Al4V. The coatings exhibited superior wear resistance than the substrate under different environments. In dry friction conditions, the friction coefficient decreased by 16.9 ~ 55.5%, and the wear rate decreased by 14.6 ~ 33.1%, compared to the substrate. In a 3.5 weight percent (wt.%) NaCl solution at room temperature, the friction coefficient decreased by 9.5 ~ 64.5%, and the wear rate decreased by 16.5 ~ 45.1%. By integrating SEM and EDS results from the worn surfaces, the alterations in wear mechanisms of the substrate and coatings were elucidated. The study demonstrates the potential application of CoCrFeNiZrx coatings in the field of marine engineering, providing a solution to extend the service life of titanium alloys in marine environments.

Effect of Hafnium Addition on the Microstructure and Property Evolutions of ZrCN Coating Prepared via Physical Vapor Deposition

Effects of HfC/PyC Core-Shell Structure Nanowires on the Microstructure and Mechanical Properties of Hf1-xZrxC Coating

Microstructure, mechanical properties and oxidation resistance of (Zr, Hf)N x coatings by magnetron co-sputtering

Effect of ZrC on the Microstructure and Properties of CrMnFeCoNi High-Entropy Alloy Coatings Prepared by a Plasma Transferred Arc Process

The Effects of Substrate Bias on the Properties of HfC Coatings Deposited by RF Magnetron Sputtering

Influences of deposition temperature, gas flow rate and ZrC content on the microstructure and anti-ablation performance of CVD-HfC-ZrC coating

Synergistic Effect of Zr and Hf Alloying on Cross Fluvial Microstructure of CoCrFeNi Eutectic High-Entropy Alloys

Effect of HfC addition on the microstructure and properties of W–4.9Ni–2.1Fe heavy alloys

Effect of C2h2 Flow Rate on the Deposition of Zr-Zrc-Zrc/Dlc Gradient Nano-Composite Film on Biomedical Niti Alloy

Effect of Zirconium Content on the Microstructure and Corrosion Behavior of As-Cast Ti-Al-Nb-Zr-Mo Alloy

Effect of Hf addition on microstructural evolution and corrosion behavior of nickel-based alloys in hydrochloric acid

Design of amorphous-nanocrystalline films of TiAlCrNbZr x multi-component alloy: The effect of Zr on the corrosion resistance and mechanical properties

Effect of ZrO2 Particles on the Microstructure and Ultrasonic Cavitation Properties of CoCrFeMnNi High-Entropy Alloy Composite Coatings

Design of Amorphous-Nanocrystalline Films of Sputtered Tialcrnbzr Multi-Component Alloy: the Effect of Zr on the Corrosion Resistance and Mechanical Properties

Fabrication and Characterization of Ni–Zr Composite Coatings Using Electrodepositing Technique

Ablation Resistance of Hf/Zr-based Multiphase Coating/matrix-Modified C/C Composites at Ultrahigh Temperatures

Synthesis, microstructural characterization and nanoindentation of Zr, Zr-nitride and Zr-carbonitride coatings deposited using magnetron sputtering

Microstructure and Anti-Ablation Performance of HfC-TaC and HfC-ZrC Coatings Synthesized by CVD on C/C Composites

Effect of Hf Addition on Initial Microstructure of (ni, Pt)Al Coating and Inhibiting the Detrimental Sulfur During High Temperature Exposure at 1150 °C

Influence of ZrB2 Nanoparticles on Microstructure and Mechanical Properties of Ni-Co Coating

Microstructure and Corrosive-Wear Properties of CoCrFeNiZrx High Entropy Alloy Coating Fabricated on Ti6Al4V by Laser Cladding