Interconnected Hollow Si/C Hybrids Engineered by the Carbon Dioxide-Introduced Magnesiothermic Reduction of Biosilica from Reed Plants for Lithium Storage
Jie Wang,Yaqi Wang,Qiwen Jiang,Jian Zhang,Huanhuan Yin,Ziqi Wang,Jiafeng Gao,Zhixia Wu,Jiazhen Liang,Songlin Zuo
DOI: https://doi.org/10.1021/acs.energyfuels.1c00836
2021-05-26
Abstract:Silicon, with its natural abundance and high gravimetric capacity, holds tremendous potential for practical Li-ion batteries (LIBs). However, the major issue related to silicon is its huge volume change during the charge/discharge processes, leading to structural degradation and instability. We report herein reed plants-derived interconnected hollow Si/C hybrids fabricated by using CO<sub>2</sub> (carbon source) in traditional magnesiothermic reduction. Both the CO<sub>2</sub> amount and HCl concentration for the extraction of SiO<sub>2</sub> play a significant role on the architecture design and rational composition of the Si/C hybrids during this new synthetic system. Significantly, the Si/C composites with 21 wt % carbon content as anodes for LIBs display a large reversible specific capacity of 1548 mAh g<sup>–1</sup> at 100 mA g<sup>–1</sup> and a superior specific capacity of 650 mAh g<sup>–1</sup> at 500 mA g<sup>–1</sup> for 200 cycles and of 1025 mAh g<sup>–1</sup> at 2000 mA g<sup>–1</sup>. The outstanding rate property and good cycling performance are ascribed to cooperativity of morphologies and structures of the Si/C composites, possessing a large pore volume and specific area, unique interconnected hollow structure, and high electrical conductivity. Additionally, such biomass-derived Si/C hybrid synthetic route with low cost and large-scale production merits probably accelerates the commercialized application of Si-based anodes for LIBs.The Supporting Information is available at ACS Publications Web site for free. . The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.1c00836?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.1c00836</a>.XRD patterns of SiO<sub>2</sub>-1, SiO<sub>2</sub>-2, SiO<sub>2</sub>-3, and SiO<sub>2</sub>-4; XRD patterns of Si/C-1, Si/C-2, Si/C-3, and Si/C-4; FE-SEM images of SiO<sub>2</sub>-1, SiO<sub>2</sub>-2, and SiO<sub>2</sub>-4; N<sub>2</sub> adsorption–desorption isotherm and pore-size distribution of Si/C-1, Si/C-2, Si/C-3, and Si/C-4; and table for specific surface area and pore volume of SiO<sub>2</sub>-1, SiO<sub>2</sub>-2, SiO<sub>2</sub>-3, and SiO<sub>2</sub>-4 (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.1c00836/suppl_file/ef1c00836_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
energy & fuels,engineering, chemical