Abstract:In a H2/N2 atmosphere, the reduction processes of Mg–Fe–O and Mg–Fe–Al–O complex oxide catalysts, derived from their hydrotalcite precursors, were studied by means of temperature-programmed reduction (TPR). In particular, the reduction process of the Mg–Fe–O samples with a Mg/Fe ratio of 1/1 and Mg–Fe–Al–O with a Mg/Fe/Al ratio of 2/1/1 were investigated in detail in combination with in situ Mössbauer spectroscopy and X-ray diffraction (XRD). For the Mg–Fe–O sample, two peaks were observed in the TPR profile with peak temperatures at 446 and 696°C, respectively, indicating that the reduction of the oxide catalyst proceeded via two stages. Mössbauer spectroscopy and XRD showed that the phases in the sample were MgFe2O4 and MgO before TPR. At the first TPR peak (446°C), MgFe2O4 was completely reduced to Mg1−xFexO. The Mössbauer spectrum of Mg1−xFexO exhibited a doublet with IS=0.83 mm/s and QS=0.87 mm/s. The second TPR peak (696°C) corresponded to the reduction of Mg1−xFexO to Fe0. For the Mg–Fe–Al–O sample, two peaks were also observed in the TPR profile with temperatures at 506 and 936°C, respectively. Mössbauer spectroscopy and XRD showed that the phases in the sample were α-Fe2O3, MgFeAlO4, and MgO before TPR. The Mössbauer spectrum of MgFeAlO4 was a doublet with IS=0.33 mm/s and QS=0.76 mm/s. At the first TPR peak (506°C), α-Fe2O3 was reduced to Fe2+ and Fe0, while MgFeAlO4 was transformed into Mg1−xFexO. The second TPR peak (936°C) corresponded to the reduction of Mg1−xFexO to metallic Fe0. Effects of the presence of magnesium and aluminum in the solid solutions on the reduction of iron species were discussed.

Thermal characterisation of alumina supported chromium and platinum–chromium catalysts

The state of metallic phase in alumina-supported platinum—chromium catalysts

Temperature Programmed Reduction of a PdCu Bimetallic Catalyst via Atmospheric Pressure in situ STEM-EDS and in situ X-Ray Adsorption Analysis

Study on Reduction Property of Cobalt Based F-T Synthesis \catalyst Supported on Alumina

Low-temperature Gas-Phase Toluene Catalytic Combustion over Modified CoCr2O4 Spinel Catalysts: Effect of Co/Cr Content and Calcination Temperature

The Interaction Between Active Phase and Support and the Tpr Characteristics on Cuo/Zro2 Catalyst

Studies on the Tpr Characteristics and Oxidation Activities of Catalysts of Cu,Ag and Cu-Ag Supported on Gamma-Al2o3

A study on the reduction behavior of silica supported iron and platinum-iron catalysts

Temperature-Programmed Reduction of NiO/Al2O3 by Biochar In Situ Generated from Citric Acid

Catalytic properties of the platinum catalyst supported on alumina modified by oxalic acid in n-heptane reforming

Effect of ZrO2 on surface oxygen performance of Mn-O/γ-Al2O3 catalyst

A study on reduction behaviors of the supported platinum–iron catalysts

Influence of thermal treatment on catalytic performance of Pd/(Ce,Zr)Ox–Al2O3 three-way catalysts

Study on the Reduction Behavior of Zirconia Supported Iron Oxide Catalysts by Temperature-Programmed Reduction Combined within SituMössbauer Spectroscopy

Studies of TPR in situ Fe-57 MBS on the reduction behavior of the gamma-Al2O3 supported iron and platinum-iron catalysts

Influence of Oxidation Temperature on Photocatalytic Activity of Cr-TiO2 Coatings by Mechanical Coating Technique

Comparative study of three-way catalytic performance over Pd/CeO2-ZrO2-Al2O3 and Pd/La-Al2O3 catalysts: New insights into microstructure and thermal stability

Effect of ZrO2 on CuO/gamma-Al2O3 catalyst in carbon monoxide oxidation

Soot oxidation and NOx reduction over BaAl2O4 catalyst

Accelerating Catalytic Oxyanion Reduction with Inert Metal Hydroxides

The Reduction of Mg–Fe–O and Mg–Fe–Al–O Complex Oxides Studied by Temperature-Programmed Reduction Combined with in Situ Mössbauer Spectroscopy