Abstract:Pitting damage severely degrades the mechanical properties of the main force-bearing member of a circular tube; it can also change its failure mode. Offshore high-strength seamless steel pipes with steel grade X52Q certified by ABS were selected for a pressure test and research. The constraint conditions of one hinged end and one fixed end were adopted to investigate the effect of the bending moment of the nodes so that any section of the circular tube can be subjected to the superposition of axial force and bending moment. Pitting craters were generated using mechanical processing methods; the effect of pitting parameters such as diameter, depth, and distribution on the mechanical properties and failure modes of circular pipes was explored. Pitting corrosion damage caused local stress concentration and the local cross-section weakening of the tube. In addition to the decline of the bearing capacity under the action of axial compression load, the failure mode of the pitting corrosion damage tube also showed differences. Increased local damage caused by the increase in the diameter of the pitting corrosion was likely to cause plastic hinges on the pits of the tube, and this changed stress conditions, failure modes, and failure locations of the components. An increase in the depth of the pitting craters resulted in a significant drop in the overall load-bearing capacity caused by local buckling. The location of pitting corrosion had negligible effect on the mechanical performance of the tube; the end distribution was more unfavourable than the centre distribution. The stress–strain distribution characteristics of the pitting area of the specimen were considerably different, and the stress concentration on the inner side of the pitting corrosion were serious and uneven. The results of the experimental analysis and several numerical examples indicated that pitting corrosion causes the pressure-bearing circular pipes with lower strength buckling to more likely suffer from an instability failure.

Investigation on failure mechanism of stiffened plates with pitting corrosion under uniaxial compression

Effect Of Corroded Surface Morphology On Ultra-Low Cycle Fatigue Of Steel Bridge Piers

Design of Vertically Stiffened Steel Plate Walls under Combined Uniaxial Compression and Shear Loads

Experimental Investigation into Flexural Buckling of Double-Limb Built-Up Plate Members under Compression

Design Approach of Stiffeners in Extended End Plate Connections and Finite Element Analysis

Experimental study on the compression mechanical behaviour of steel pipes with mechanically induced pitting corrosion

Compressive Behaviour of Corroded Thin-Walled Circular Section Steel Stub Columns

Experimental Investigation of Corroded Stud Shear Connectors Subjected to Fatigue Loading

Experimental Investigation and Design of Corroded Stud Shear Connectors

Compression capacity of corroded plates with three sides simply supported and one side free

Experimental and Numerical Study on Failure Behaviors of Composite Grid Stiffeners under Tensile and Flexural Loading

Ultimate strength of stiffened panels with a crack and pits under uni-axial longitudinal compression

Probabilistic constitutive model for corroded structural steel with stochastic pits under monotonic tension

Experimental and numerical study of residual ultimate strength of hull plate subjected to coupled damage of pitting corrosion and crack

Monotonic and fatigue behavior of steel-concrete composite beams subjected to corrosion

Static and Fatigue Behavior of Steel-Concrete Composite Beams with Corroded Studs

Ultimate torsional strength assessment of large deck opening stiffened box girder subjected to pitting corrosion

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Experimental studies on crack propagation and accumulative mean strain of cracked stiffened plates under low-cycle fatigue loads

Surface topography and stress concentration analysis for corroded high strength steel plate

Peridynamic Investigation of Stress Corrosion Cracking in Carbon Steel Pipes