Abstract:Magnesium hydride (MgH2) offers large capacity for hydrogen storage, but poor thermodynamics and kinetics for releasing hydrogen. In this work, the novel 1D bamboo-shaped carbon nanotubes (BCNTs) are firstly used as carriers for the self-assembly of MgH2 (denoted as MgH2@BCNTs). The high specific surface area (262.3 m(2)g(-1)) and large diameter (over 80 nm) of BCNTs contribute to extremely high loading capacity (76.8 mass fraction), small particle size (15-20 nm) and uniform distribution of MgH2 nanoparticles (NPs). The well-defined MgH2@BCNTs shows remarkably improved thermodynamics and kinetics for H-2 adsorption and desorption. In particular, it starts to release hydrogen at about 220 degrees C, near 170 degrees C lower than that of the commercial MgH2, as well it tends to be hydrogenated even at a relatively low temperature of 100 degrees C by absorbing 3.56 wt% H-2. Moreover, a reversible capacity up to 5.79 wt%, including the "dead weight" of BCNTs, and is well maintained after 10 cycles. The dehydrogenation E-a and Delta H of MgH2@BCNTs can be reduced to 97.97 kJ/mol and 68.92 kJ/mol, which are 111.24 kJ/mol and 6.07 kJ/mol lower than those of the commercial MgH2, respectively. By high pressure densification treatment, the MgH2@BCNTs system achieves an exceptional volumetric capacity up to 65.90 g/L without obvious performance degeneration, resulting from the special structure of BCNTs with inner intervals which works as supports under ultra-high pressure of 750 MPa. Our innovative design of 1D BCNTs supporting MgH2 NPs with high loading weight offers new strategy to synchronously improve the gravimetric and volumetric capacity, as well as the hydrogen storage kinetics and thermodynamics of the nanoconfinement system in the future.

Novel core–shell structured MgH 2 /AlH 3 @CNT nanocomposites with extremely high dehydriding–rehydriding properties derived from nanoconfinement

Synthesis and characterization of multiwalled carbon nanotube/CdS core/shell heterostructures

Carbon composite support improving catalytic effect of NbC nanoparticles on the low-temperature hydrogen storage performance of MgH2

The Dehydrogenation Mechanism and Cycling Property of MgH 2 Modified by CoB/CNTs Addition

Ni-CNTs as an efficient confining framework and catalyst for improving dehydriding/rehydriding properties of MgH2

CNTs Decorated with CoFeB As a Dopant to Remarkably Improve the Dehydrogenation/rehydrogenation Performance and Cyclic Stability of MgH2

Remarkable Hydrogen Desorption Properties and Mechanisms of the Mg2FeH6@MgH2 Core–shell Nanostructure

Enhanced Hydrogen Storage Properties of MgH2 by the Synergetic Catalysis of Zr0.4Ti0.6Co Nanosheets and Carbon Nanotubes

Core–shell Co@C catalyzed MgH2: enhanced dehydrogenation properties and its catalytic mechanism

ZIF-67 derived Co@CNTs nanoparticles: Remarkably improved hydrogen storage properties of MgH2 and synergetic catalysis mechanism

Enhancing hydrogen storage properties of MgH2 by core-shell CoNi@C

Mg–TM (TM: Ti, Nb, V, Co, Mo or Ni) core–shell like nanostructures: synthesis, hydrogen storage performance and catalytic mechanism

Novel 1D Carbon Nanotubes Uniformly Wrapped Nanoscale MgH2 for Efficient Hydrogen Storage Cycling Performances with Extreme High Gravimetric and Volumetric Capacities

Highly-dispersed Nano-Tib2 Derived from the Two-Dimensional Ti3CN MXene for Tailoring the Kinetics and Reversibility of the Li-Mg-B-H Hydrogen Storage Material

MgH 2 @Mg(BH 4 ) 2 Core-Shell-like Nanostructures: Synthesis, Hydrolysis Performance, and Promotion Mechanism

The Synthesis and Electrochemical Performance of Core-Shell Structured Ni-Al Layered Double Hydroxide/carbon Nanotubes Composites

Enhanced hydrogenation and hydrolysis properties of core-shell structured Mg-MOx (M = Al, Ti and Fe) nanocomposites prepared by arc plasma method

A Novel Method to Fabricate CNT/Mg–6Zn Composites with High Strengthening Efficiency

In Situ Formed Ti/Nb Nanocatalysts within a Bimetal 3D MXene Nanostructure Realizing Long Cyclic Lifetime and Faster Kinetic Rates of MgH 2

Synthesis of core-shell α-AlH3@Al(OH)3 nanocomposite with improved low-temperature dehydriding properties by mechanochemical mixing and ionic liquid treatment

A facile and novel synthetic route to core–shell Al/Co nanocomposites