Novel fabrication of rod-like CoAl2O4/halloysite hybrid pigment derived from Co-MOF/nano-clay and mechanism exploration
Qing Sun,Jingfeng Zhao,Zhibo Hu,Jian Zhang,Jun Yan,Jiawei Sheng
DOI: https://doi.org/10.1016/j.dyepig.2022.110216
IF: 5.122
2022-05-01
Dyes and Pigments
Abstract:In this work, we successfully report the design and synthesis of rod-like CoAl2O4/halloysite hybrid pigment from zeolitic imidazolate framework-67 (ZIF-67, a Co-based MOF) and tubular halloysite via a facile two-step route for the first time. The as-prepared nanostructures were thoroughly characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared reflection (FTIR Spectroscopy), thermogravimetric and differential scanning calorimetry (TG-DSC), X-ray photoelectron spectrometer (XPS), ultraviolet–visible spectrometry (UV–vis) and CIE L* a* b* colorimetric method. XRD patterns indicated that the presence of CoAl2O4 spinel was observed at various temperatures ranging from 800 to 1100 °C. The SEM and TEM images showed that the nano-pigment has a rod-like hybrid structure composed of nano CoAl2O4 particles and SiO2. The color performance of the fabricated pigments was evaluated and given suitable color coordinates (L* = 44.72, a* = −14.40, b* = −37.83) and (L* = 42.57, a* = −7.68, b* = −41.14) at the calcination temperature of 1100 °C for 2 h and 3 h, respectively. The mechanism study indicated that these composites were formed by Co3O4 derived of ZIF-67 as highly active cobalt source and Al2O3 decomposed from halloysite substrate as aluminum source. In addition, the corrosion resistance test showed that the CoAl2O4 composites retain crystalline stability, almost no color deviation in CIE chromatic system even after 1 M HCl leaching. Furthermore, the CoAl2O4/halloysite exhibited excellent thermal and suspension stability, which indicated it could be a promising candidate for ceramic glazes and water-borne coatings. These findings provide insight into a new strategy for the synthesis of clay mineral-based ceramic pigment.
engineering, chemical,chemistry, applied,materials science, textiles