Abstract:Bi2(TeSe)3 is a dominant n-type thermoelectric material used in commercial applications. However, its toxicity and rarity hamper further large-scale industrial applications. Herein, we develop a Ag8SiSe6-based composite as a promising n-type semiconductor with the advantages of nontoxicity and elemental abundance. Ag8SiSe6 composites with Ag2Se and Si nanoprecipitation are fabricated by a unique precipitation reaction sensitive to the hot pressing process. The energy-filtering effect between these phases optimizes electrical resistivity (∼14.59 μΩ·m) and the Seebeck coefficient (above −150 μV·K–1) of the composites, resulting in a maximum power factor of ∼1772 μW·m–1·K–2(@125 °C), which is the highest value in an argyrodite system near room temperature. Nanoprecipitation of Ag2Se and Si can also scatter more phonons and further reduce the lattice thermal conductivity to 0.20 W·m–1·K–1. As a result, a maximum ZT value of ∼0.9 (@125 °C) and an average ZT value of ∼0.7 (25–200 °C) are obtained in the composite with 12 vol % Ag2Se and 0.23 vol % Si, which is sintered at 525 °C. These thermoelectric properties are comparable to those of a commercial n-type Bi2Te3 compound. In addition, the Ag8SiSe6 composite has robust mechanical properties (Vickers hardness of >110 HV and bending strength of 70.6 MPa), much better than those of other thermoelectric compounds, because of which Ag8SiSe6 has great commercial application as an alternative to Bi2Te3-based compounds.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c15877?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c15877</a>.Remaining details of thermal conductivity calculation, band structure calculation, and the energy-level diagram of Ag8SiSe6, Ag2Se, and Si (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c15877/suppl_file/am0c15877_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Ag2Q‐based (Q = S, Se, Te) Silver Chalcogenide Thermoelectric Materials

Are Cu2Te‐Based Compounds Excellent Thermoelectric Materials?

Microstructures and Thermoelectric Properties of GeSbTe Based Layered Compounds

Superior thermoelectric properties of ternary chalcogenides CsAg5Q3 (Q = Te, Se) predicted using first-principles calculations

Incommensurately Modulated Structure in AgCuSe‐Based Thermoelectric Materials for Intriguing Electrical, Thermal, and Mechanical Properties

General surfactant-free synthesis of binary silver chalcogenides with tuneable thermoelectric properties

High‐Performance AgSbTe2 Thermoelectrics: Advances, Challenges, and Perspectives

Ecofriendly Highly Robust Ag 8 SiSe 6 -Based Thermoelectric Composites with Excellent Performance Near Room Temperature

High-performance and stable AgSbTe 2 -based thermoelectric materials for near room temperature applications

High‐Entropy Cubic Pseudo‐Ternary Ag 2 (S, Se, Te) Materials With Excellent Ductility and Thermoelectric Performance

Study of the Defect Chemistry in Ag 2 Q (Q = S, Se, Te) by First-principle Calculations

Engineering of Thermoelectric Composites Based on Silver Selenide in Aqueous Solution and Ambient Temperature

Unlocking the Potential of Coinage-Based Quaternary Chalcogenides for Thermoelectricity

Structural transformation and thermoelectric performance in Ag2Te1−Se solid solution

Silver-Based Intermetallic Heterostructures in Sb2Te3 Thick Films with Enhanced Thermoelectric Power Factors

Optimized Thermoelectric Performance and Plasticity of Ductile Semiconductor Ag2S0.5Se0.5 Via Dual‐Phase Engineering

First-Principles Calculations of Thermoelectric Transport Properties of Quaternary and Ternary Bulk Chalcogenide Crystals

Prefer‐Oriented Ag2Se Crystal for High‐Performance Thermoelectric Cooling

Dual Alloying Enables High Thermoelectric Performance in AgSbTe2 by Manipulating Carrier Transport Behavior

Thermoelectric materials with crystal-amorphicity duality induced by large atomic size mismatch

: A potential thermoelectric material with promising electronic transport