Abstract:Oxide dispersion strengthened (ODS) FeCrAl alloys were prepared by mechanical alloying (MA) and spark plasma sintering (SPS) technology. To reveal the high temperature oxidation properties, ODS FeCrAl alloys were exposed to dry air for various times (1h, 4h, 10h, 20h, 45h, 70h, and 100h) at 1100 °C to investigate the microstructure evolution. The results illustrated that a flat and adherent alumina scale was gradually thickened on the alloy substrate with the increase of the oxidation time. In particular, it was observed that large-size reactive element (RE) oxides were inclined to be associated with cavities close to the gas interface and these cavities were progressive evolution to be larger-size pores with longer exposure time, while tiny RE oxides were not dispersed with cavities after 100h oxidation. In addition, α-Al2O3 with a double-scale structure were mainly composed of inner columnar grains and outer equiaxed grains, as well, the growth of α-Al2O3 scales illustrated that the oxidation rate decreased with oxidation reaction proceeding. For one thing, Ti segregation along grain boundaries (GBs) near the gas interface decreased the outward diffusion of the Al ions to weaken the oxidation rate. Furthermore, the gradual coarsening of columnar grains near the alloy substrate implied a longer diffusion path of O atoms, thereby accounting for slower oxidation process. To sum up, ODS FeCrAl alloys with thinner oxide thickness demonstrated the superior oxidation resistance than other materials, which would make it one of the promising candidate structural materials applicated in accident-tolerant fuel (ATF) cladding materials.

Grain Size Effect and Spinel Transition for Alumina Scale Thermally Grown on Rare Earth–Mg Codoped FeCrAl Alloy

Oxidation Mechanism of Three Fe-Al Alloys with and Without Addition of 0.1 At% Yttrium at 800 °C

Spallation Behaviour of Alumina Scale Formed on FeCrAlY Alloy After Isothermal Oxidation

Effect of Grain Size on Oxidation Behavior of Fe-40ni-15cr Alloys

Contribution of Sc Doping to the Growth and Adhesion of Alumina Scale on AlCoCrFeNi High-Entropy Alloy

Effect of Pt Doping on Oxide Scale Formation on Yttria-Dispersion FeCrAl Alloy at 1200℃

High-resolution Characterization Reveals the Role of Al Content in the Evolution of Oxide Scales Formed on Alumina-Forming Alloy Exposed to Supercritical Water

Effect of Cooling Rate and Substrate Thickness on Spallation of Alumina Scale on Fecralloy

Effect of Grain Size on the Oxidation of Fe–13Cr–5Ni Alloy at 973K in Ar–21vol%O2

Effect of Al addition on the grain refinement and mechanical properties of as-cast Mg–5Y–4Sm alloys

Effect of Alloyed Lu, Hf and Cr on the Oxidation and Spallation Behavior of NiAl

Alloying Elements Effect on the Recrystallization Process in Magnesium-Rich Aluminum Alloy

Effects of Manganese And/Or Carbon on the Grain Refinement of Mg-3al Alloy

Influence of the Temperature and Duration of the Annealing on the Lattice Structure and Growth of the Mg–Al Spinel Layer

Effect of Al Addition on Grain Refinement and Phase Transformation of the Mg-Gd-Y-Zn-Mn Alloy Containing LPSO Phase

Wrinkling Behavior of Alumina Scales Formed During Isothermal Oxidation of Fe–Al Binary Alloys

Effect of grain boundaries on the formation of oxide scale in Fe–Cr alloy for SOFCs

Microstructure Evolution and Oxidation Resistance Properties of Oxide Dispersion Strengthened FeCrAl Alloys at 1100 °C

The importance of grain boundaries on the reactive elements effect in β-NiAlHf alloy

Effect of Grain Size on Tensile Deformation Behavior of Nano-Polycrystalline Al and Al–Mg Alloys with Grain Boundary Segregation of Mg

Designing Ultrastrong and Thermally Stable FeCrAl Alloys with the Fine-Grained Structure