Abstract:To improve the poor membrane-forming ability of polymer containing sterically-protected organic cations with the excellent alkaline stability, a series of robust and crosslinked poly(2,6-dimethyl-1,4-phenylene oxide)s (PPO) anion exchange membranes (AEMs) with bulky and chemically stable imidazolium cations was prepared by quaternization with C1,C3,C4-substituted imidazole and crosslinking reaction via "thiol-ene" chemistry. Compared to the uncrosslinked counterpart, the crosslinked AEMs showed excellent film-forming properties with the highest of tensile strength of 53.2 MPa, probably owing to the increased entanglement interactions in polymer chains that may in turn result in the controlled the water uptake and dimensional stability of the AEMs. Moreover, by using two different crosslinkers, water uptake of the resulting AEMs could be effectively tuned. The crosslinked AEM had a water uptake of 12.8 wt% with the ion exchange capacity (IEC) of 1.27 meq./g when using a hydrophilic dithiol as the crosslinker, which was almost twice than that for the membrane with hydrophobic crosslinker AEM (water uptake was 6.6 wt%, IEC = 1.28 meq./g). The higher water uptake further contributed to high ionic transport with bromide conductivity of 11.2 mS/cm at 20 degrees C in water and 24.8 mS/cm at 80 degrees C. The excellent alkaline stability of these materials was demonstrated by the fact that, more than 90.4% of bromide conductivity and 60.5% of tensile strength was retained after 1000 h immersion in 1 M NaOH at 80 degrees C, due to the presence of crosslinked networks and alkali-resistant sterically-protected imidazolium. Furthermore, we compared the AEM fuel cell performance and durability of the membrane electrode assembly (MEA) using the crosslinked and uncrosslinked bulky imidazolium-functionalized PPO copolymers as ionomers in catalyst layers. A higher peak power density of 200 mW/cm(2) at a current density of 475 mA/cm(2) and improved short-term durability (20.5 h) under a constant current density of 200 mA/cm(2) at 60 degrees C were obtained for the membrane electrode assembly with the crosslinked ionomer. These results suggest that crosslinking of anion conductive materials with stable sterically-protected organic cations is a facile and effective strategy to prepare the robust and alkaline stable AEMs for high-performance alkaline fuel cells.

Multi-imidazonium cationic cluster cross-linked hydrogenated benzonorbornadiene diblock copolymer anion exchange membrane for improving conductivity and mitigating swelling

Multi-imidazolium Cationic Clusters Cross-Linked Hydrogenated Benzonorbornadiene Diblock Copolymer Anion Exchange Membranes for Improving Conductivity and Mitigating Swelling

Poly(olefin)-Based Anion Exchange Membranes Prepared Using Ziegler–Natta Polymerization

Towards high conductivity and stability diblock poly(norbornene)s-based anion exchange membranes crosslinked with alkyl quaternary ammonium cationic clusters

Hydrogenated Diblock Copoly(norbornene)s Bearing Triimidazolium Anion Exchange Membranes with Enhanced Alkaline Stability for Fuel Cells

Novel Self-Cross-linked Multi-Imidazolium Cations Long Flexible Side Chains Triblock Copolymer Anion Exchange Membrane Based on ROMP-type Polybenzonorbornadiene

Highly Conductive and Water-Swelling Resistant Anion Exchange Membrane for Alkaline Fuel Cells

Synthesis of Halogenated Benzonorbornadiene Monomer and Preparation of Self-Crosslinking Bisimidazole Cationic Functionalized Benzonorbornadiene Triblock Copolymer Anion Exchange Membrane

Partially Fluorinated, Multication Cross-Linked Poly(arylene Piperidinium) Membranes with Improved Conductivity and Reduced Swelling for Fuel Cell Application

Olefin Metathesis-Crosslinked, Bulky Imidazolium-Based Anion Exchange Membranes with Excellent Base Stability and Mechanical Properties

Polybenzimidazole Ultrathin Anion Exchange Membrane with Comb-Shape Amphiphilic Microphase Networks for a High-Performance Fuel Cell

Microcrystalline-Induced Physical-Cross-linking Toward a High Performance Hyper-Branched Anion Exchange Membrane

High Ion Conductivity and Diffusivity in the Anion Exchange Membrane Enabled by Tethering with Multication Strings on the Poly(biphenyl Alkylene) Backbone

Comb-shaped anion exchange membrane with segmented hydrophilic/hydrophobic side chain

Anion Exchange Membranes with "Rigid-Side-chain" Symmetric Piperazinium Structures for Fuel Cell Exceeding 1.2 W Cm−2 at 60 °C

Anion Conductive Membrane Performance Facilitation Via Tethering Flexible with Rigid Backbones Using Oscillational Chain

Durable Multiblock Poly(biphenyl Alkylene) Anion Exchange Membranes with Microphase Separation for Hydrogen Energy Conversion

Anion exchange membranes with branched ionic clusters for fuel cells

Microcrystalline induced physical-crosslinking towards high performance branched anion exchange membrane

Interpenetrating Anion Exchange Membranes Using Poly(1-Vinylimidazole) As Bifunctional Crosslinker for Fuel Cells

Enhancement of the Mechanical Properties of Anion Exchange Membranes with Bulky Imidazolium by "Thiol-Ene" Crosslinking