Simultaneously enhancing heat resistance and mechanical performance for phthalonitrile through in-situ formation of inorganic protective layer derived from low melting point oxide

Zi-long Wang,Xin Zhou,Kun Zheng,Ying Guo,Jun Wang,Wen-bin Liu,Heng Zhou,Tong Zhao

DOI: https://doi.org/10.1016/j.compositesa.2023.107740

2023-08-12

Abstract:Simultaneously improving the heat resistance and mechanical properties for phthalonitrile resin using inorganic filler with high melt-point remains a challenge owing to the difficult formation of a ceramic protective layer to enhance the heat resistance of phthalonitrile resin. Here, heat resistance and mechanical performance of the phthalonitrile resin were both improved by introducing low melt-point molten oxide with temperature-adaptable geometry. The as-prepare phthalonitrile/molten oxide blend exhibited high temperature of 5% mass loss of 525.2 o C and 554.6 o C at air and N 2 atmosphere, respectively, and high mass residue of 81.9% at 900 o C (in N 2 ). The enhanced thermal stability of blend was attributed to the formation of protective layer from temperature-adaptable capacity of oxide. For the carbon fiber fabric reinforced blend composite, the flexural strength was improved by 29.1%, 59.6%, and 54.6% compared with pristine carbon fiber fabric reinforced phthalonitrile composites at room temperature, 400 o C and 500 o C, respectively.

materials science, composites,engineering, manufacturing