Abstract:In this study, a natural zeolite supported Co-B catalyst (Co-B/Zeolite) with a Co content of 10 wt.% was prepared by impregnation and chemical reduction method to release hydrogen gas from an alkaline sodium borohydride (NaBH 4 ) solution. The synthesized catalyst was characterized with various characterization techniques, including X-ray diffraction (XRD), X-ray fluorescence (XRF), inductively coupled plasma mass spectroscopy (ICP-MS), Brunauer–Emmett–Teller (BET), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), Fourier transform infrared (FTIR), and X-ray photoelectron spectroscopy (XPS), etc. It was found that the BET specific surface area of Co-B/Zeolite (26.03 m 2 g −1 ) was roughly double that of the zeolite (13.12 m 2 g −1 ). The Co ratio in the catalyst was found to be 12.02 wt.% by EDX analysis. ICP-MS examination of the catalyst revealed a B/Co atomic ratio of 0.64. No peaks associated with Co-B were observed in the XRD pattern of the catalyst, indicating the amorphous nature of the component. Parameters that have significant effects on the hydrolysis reaction, such as catalyst amount, sodium hydroxide and sodium borohydride concentrations, and reaction temperature, were investigated. The hydrogen generation rate (HGR) was found to be 1732 mL min −1 g cat −1 in the presence of 100 mg of Co-B/Zeolite in 5 wt.% NaOH and 5 wt.% NaBH 4 solution at 50 °C. The experimental results were well fitted to the zero-order kinetic model ( k 0 = 0.0296–0.1619 mol min −1 g cat −1 for 20–50 °C). The activation energy ( E a ) of the catalytic reaction was found to be 44.98 kJ mol −1 . Meanwhile, the reusability evaluations showed that the catalyst preserves high stability and can still sustain 73% of its initial activity after 5 catalytic cycles.

Preparation of an efficient and reusable cobalt doped vermiculite ore catalyst for hydrogen production from sodium borohydride

Efficient Hydrogen Generation From The Nabh4 Hydrolysis By Cobalt-Based Catalysts: Positive Roles Of Sulfur-Containing Salts

Efficient and Stable Co-B Catalyst Supported on Natural Zeolite for Hydrogen Generation from Hydrolysis of Alkaline NaBH4 Solution

A highly active Co-B catalyst for hydrogen generation from sodium borohydride hydrolysis

Preparation of Co3−xCaxO4 nanostructure catalyst for improved hydrogen production from sodium borohydride

Magnetically Recovered Co and Co@Pt Catalysts Prepared by Galvanic Replacement on Aluminum Powder for Hydrolysis of Sodium Borohydride

A New Reactivation Method Towards Deactivation of Honeycomb Ceramic Monolith Supported Cobalt–molybdenum–boron Catalyst in Hydrolysis of Sodium Borohydride

Catalytic Hydrogen Evolution of NaBH4 Hydrolysis by Cobalt Nanoparticles Supported on Bagasse-Derived Porous Carbon

Electrospun Co Nanoparticles@PVDF-HFP Nanofibers as Efficient Catalyst for Dehydrogenation of Sodium Borohydride

Enhancing hydrogen generation from sodium borohydride hydrolysis and the role of a Co/CuFe2O4 nanocatalyst in a continuous flow system

Ultrafine cobalt nanoparticles supported on carbon nanospheres for hydrolysis of sodium borohydride

Cobalt Phosphide Nanowall Arrays Supported on Carbon Cloth: an Efficient Monolithic Non-Noble-metal Hydrogen Evolution Catalyst

Hydrogen generation from catalytic hydrolysis of sodium borohydride solution using Cobalt–Copper–Boride (Co–Cu–B) catalysts

Evaluation of a Cobalt–molybdenum–boron Catalyst for Hydrogen Generation of Alkaline Sodium Borohydride Solution–aluminum Powder System

Ion exchange resin supported cobalt boride as highly efficient catalyst for the hydrolysis of a concentrated alkaline stabilized sodium borohydride solution: A catalyst de-/reactivation study

Cobalt-based coordination polymer-derived hexagonal porous cobalt oxide nanoplate as an enhanced catalyst for hydrogen generation from hydrolysis of borohydride

Study of Cobalt Boride-Derived Electrocatalysts for Overall Water Splitting

Boride-Mediated Synthesis of Highly Active Cobalt-Based Electrocatalyst for Alkaline Hydrogen Evolution Reaction

Calcium Cobaltate: a Phase-change Catalyst for Stable Hydrogen Production from Bio-glycerol

Carbon nanospheres supported bimetallic Pt-Co as an efficient catalyst for NaBH4 hydrolysis

Copper(0) nanoparticles supported on silica-coated cobalt ferrite magnetic particles: cost effective catalyst in the hydrolysis of ammonia-borane with an exceptional reusability performance