Abstract:In this study, a series of cobalt-based spinel ferrites catalysts, including nickel, cobalt, zinc, and copper ferrites, were synthesized using the sol–gel auto-combustion method followed by a chemical reduction process. These catalysts were employed for accelerating hydrogen generation via the sodium borohydride hydrolysis process. A continuous stirred tank reactor was used to perform catalytic reactor tests. All samples were subjected to analysis using XRD, FESEM, EDX, FTIR, and nitrogen adsorption–desorption techniques. The results revealed that the cobalt-based copper ferrite sample, Co/Cu-Ferrite, exhibited superior particle distribution, and porosity characteristics, as it achieved a high hydrogen generation rate of 2937 mL/min.g cat . In addition, the higher electrical donating property of Cu-Ferrite which leads to the increase in the electron density of the cobalt active sites can account for its superior performance towards hydrolysis of NaBH 4 . Using the Arrhenius equation and the zero-order reaction calculation, activation energy for the sodium borohydride hydrolysis reaction on the Co/Cu-Ferrite catalyst was determined to be 18.12 kJ/mol. This low activation energy compared to other cobalt-based spinel ferrite catalysts confirms the catalyst's superior performance as well. Additionally, the outcomes from the recycling experiments revealed a gradual decline in the catalyst's performance after each cycle during 4 repetitive cycles. The aforementioned properties render the Co/Cu-Ferrite catalyst an efficient catalyst for hydrogen generation through NaBH 4 hydrolysis.

A highly active Co-B catalyst for hydrogen generation from sodium borohydride hydrolysis

Efficient Hydrogen Generation From The Nabh4 Hydrolysis By Cobalt-Based Catalysts: Positive Roles Of Sulfur-Containing Salts

Ultrafine cobalt nanoparticles supported on carbon nanospheres for hydrolysis of sodium borohydride

Nickel- and Cobalt-Based Catalysts for Hydrogen Generation by Hydrolysis of Borohydride

Highly Efficient Ferromagnetic Co B O Catalyst for Hydrogen Generation

Highly Active and Robust Catalyst: Co2B-Fe2B Heterostructural Nanosheets with Abundant Defects for Hydrogen Production

Multifunctional Co-B-O@Co<sub>x</sub>B catalysts for efficient hydrogen generation

Ion exchange resin supported cobalt boride as highly efficient catalyst for the hydrolysis of a concentrated alkaline stabilized sodium borohydride solution: A catalyst de-/reactivation study

Bacterial cellulose derived carbon as a support for catalytically active Co–B alloy for hydrolysis of sodium borohydride

Graphene-Modified Co-B-P Catalysts for Hydrogen Generation from Sodium Borohydride Hydrolysis

Development of Al2O3-supported nanobimetallic Co-La-B catalyst for boosting hydrogen release via sodium borohydride hydrolysis

High-Surface-Area Co-Cu-B Monolithic Self-Supported Catalyst for Efficient Sodium Borohydride Hydrolysis

Synthesis of highly stable cobalt nanorods anchored on a Ti4N3Tx MXene composite for the hydrolysis of sodium borohydride

Synthesis of a Novel Co-B/CTAB Catalyst Via Solid-state-reaction at Room Temperature for Hydrolysis of Ammonia-borane

Carbon nanospheres supported bimetallic Pt-Co as an efficient catalyst for NaBH4 hydrolysis

Ultrafine Amorphous Co–Fe–B Catalysts for the Hydrolysis of NaBH4 Solution to Generate Hydrogen for PEMFC

Magnetically Recovered Co and Co@Pt Catalysts Prepared by Galvanic Replacement on Aluminum Powder for Hydrolysis of Sodium Borohydride

Synergistic effect of Co catalysts with atomically dispersed CoN x active sites on ammonia borane hydrolysis for hydrogen generation

Kinetically promoted hydrogen generation by Ru nanoparticles decorated CoB2O4 on mesoporous carbon spheres with rich oxygen vacancies for NaBH4 hydrolysis

Enhancing hydrogen generation from sodium borohydride hydrolysis and the role of a Co/CuFe2O4 nanocatalyst in a continuous flow system

Catalytic Behavior of Carbon Supported Ni–B, Co–B and Co–Ni–B in Hydrogen Generation by Hydrolysis of KBH4