Abstract:Fluoride-upconversion transparent ceramic materials doped with Er ions have attracted extensive interest due to their higher stability, lower phonon energy, and higher upconversion efficiency. xEr:Sr5(PO4)3F (S-FAP) (x=0.5–5 at%) transparent ceramics have been synthesized by hot pressing sintering in this work, and the maximum optical transmittance of the sample reached 74.52 and 82.45% at 500 and 1000 nm, respectively. The XRD results of the powder and ceramic samples were consistent with the diffraction characteristics of the hexagonal S-FAP crystal structure. The SEM and TEM images of powder revealed that the morphology of the sample was composed of mostly rice grains with a diameter of around 20 nm. The XPS and EDS results confirmed the presence of Er3+ and the uniform distribution of Er elements. The thermally etched surface and cross section of ceramics revealed residual pores as the most important scattering source, and the SEM images of the ceramics show that Er doping can obviously promote the growth of the average grain size of S-FAP transparent ceramics. Furthermore, the upconversion luminescence characteristics and fluorescence lifespan of S-FAP transparent ceramics with varied Er doping concentrations were examined, as well as the upconversion luminescence process. The findings in this work indicate that Er:S-FAP transparent ceramics can be employed as a potential upconversion fluorescent material in display technology, biomedicine, temperature sensing, and other applications.

Conventional HP sintering of asymmetric hexagonal structure Yb 3+ ‐doped Sr 5 (PO 4 ) 3 F transparent ceramic without additives

Transparent hexagonal Yb:Sr5(PO4)3F ceramics fabricated by hot pressing sintering with LiF doping

Fabrication, microstructure and upconversion luminescence properties of Er:Sr5(PO4)3F transparent nanostructured ceramics

Microstructure and Luminescence of Yb3+-doped Fluorosilicate Glass Ceramics

Synthesis and Crystal Structure of Yb-doped S-FAP

Microstructure and laser performance of fine-grained Yb:CaF 2 transparent ceramics prepared by two-step sintering

Densification and microstructure evolution of hot-pressed Er:SrF2 transparent ceramics

Fabrication, microstructure and properties of transparent Yb:Y2O3 ceramics from co-precipitated nanopowders

Microstructural, spectroscopic and mechanical properties of hot-pressed Er:SrF2 transparent ceramics

Optical, thermal properties, and hydrolysis resistance of transparent YF 3 -doped CaO ceramics fabricated by vacuum sintering

Microstructure and laser emission of Yb:CaF2 transparent ceramics fabricated by air pre-sintering and hot isostatic pressing

Synthesis of Nd3+ Doped Nano-Crystalline Yttrium Aluminum Garnet (YAG) Powders Leading to Transparent Ceramic

Achieving fabrication of highly transparent Y 2 O 3 ceramics via air pre‐sintering by deionization treatment of suspension

Fabrication of Yb,La:CaF2 transparent ceramics by air pre-sintering with hot isostatic pressing

Structure and Spectral Properties of NaY<sub>2</sub>F<sub>7</sub>:Eu<SUP>3+</SUP>/Eu<SUP>2+</SUP> Transparent Glass-Ceramics

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Effect of Cr3+ Doping Concentration on the Microstructure, Mechanical Properties and Optical Properties of Cr3+: SrF2 Transparent Ceramics

Fabrication and optical characterizations of hot-pressed transparent SrF2/Nd:SrF2/SrF2 composite ceramic

Sintering and optical quality of highly transparent yb‐doped yttrium lanthanum oxide ceramics

Fabrication and spectral properties of Dy: SrF2 transparent ceramics

Fabrication, microstructure and laser performance of Yb3+ doped CaF2-YF3 transparent ceramics