Development of reversibly photo-crosslinkable water-stable poly(2-ethyl-2-oxazoline) nanofibers via functionalization with cinnamoyl moieties

Olmo frateur,Jana Becelaere,Ronald Merckx,Joachim F. R. Van Guyse,Martin Purino,Richard Hoogenboom,Karen De Clerck
DOI: https://doi.org/10.1016/j.eurpolymj.2024.113076
IF: 6
2024-05-03
European Polymer Journal
Abstract:Poly(2-ethyl-2-oxazoline) (PEtOx) is a potent member of the versatile poly(2-oxazoline) polymer platform with its high hydrophilicity that could be beneficial in numerous biomedical applications, especially in the form of a nanofibrous membrane. However, its water-solubility limits its application in situations where a stable, nanofibrous morphology is required in aqueous environments. The present work offers a straightforward route towards water-stable PEtOx-based nanofibrous membranes, via post-polymerization functionalization with cinnamoyl moieties (PEtOx-Cin) and photo-crosslinking of the electrospun membranes. It is shown that a UVB treatment does not significantly affect the nanofibrous morphology, while successfully inducing the cinnamoyl dimerization process and hence the formation of a polymeric network, as evidenced by spectral analysis. The hereby crosslinked PEtOx-based nanofibers exhibit a prolonged water-stability (at least 45 days), while, interestingly, intermediate irradiation times yield the best results. Full disintegration of the photo-crosslinked nanofibers in aqueous media could be achieved by subsequent UVC exposure. This is not only due to decrosslinking of the cinnamoyl dimers, but also due to partial degradation of the polymeric backbone. The investigation of UVB/UVC exposure on pure PEtOx nanofibrous membranes confirmed the photo-degradation of the polymeric backbone by a significant decrease in molar mass as observed by size exclusion chromatography and supported by spectral analysis. The hereby proposed, straightforward route for reversible crosslinking of PEtOx-based nanofibrous membranes and their accessible disintegration will contribute to the promotion of these materials in biomedical applications where a water-stable, nanofibrous morphology combined with high hydrophilicity and easy removal is required.
polymer science
What problem does this paper attempt to address?