Abstract:Large-scale nonequilibrium molecular dynamics simulation is used to study the effect of grain size and Cr segregation at the twin boundary (TB) on the spalling fracture mechanism of nickel based alloys. In particular, loading waves are designed so that the maximum tensile stress first appears in the grain interior for all the crystals with different grain sizes. In contrast to traditional understandings, no monotonous relationship between the spall strength and the grain size appears in our results. The spall strength is found to depend on the wave attenuation distance measured from the first maximum tensile stress position to the spalled TB as well as the accompanied microstructure evolutions. The number of spalling plane increases with the increase of TB or the decrease of the grain size. As the grain size continues to decrease, a greater impact strength is required to cause spallation fracture at multiple TBs. In this case, the spall strength becomes insensitive to the first maximum tensile stress position. With the increment of solute atom concentration, the number of the spalling plane increases when the solution is segregated. But it decreases when the solution is uniformly distributed. Such a result is explained by segregation-enhanced energy dissipation and interactions between the waves and the microstructures nearby TBs. In particular, the shock wave would induce a local lattice reorientation nearby the TB depending on its segregation degree and the lattice reorientation would modify the slip manner of stacking faults and, thus, affect void nucleation and growth. The lattice reorientation would also contribute to the generation of sub-grain boundaries inside the grains in terms of the movement of stacking faults. Void nucleation at the sub-GB is the main cause of fracture at the grain interior.

Synergy of Spall Strength and Toughness in Nanograined Metals

Damage Characteristics of Aluminum Nanorod under Hypervelocity Impact

Micromechanical Simulation of Fracture Behavior of Nanostructured Metals with Bimodal Grain Size Distribution

Simulation of Ballistic Performance of Coarse-Grained Metals Strengthened by Nanotwinned Regions

Micromechanical simulation of fracture behavior of bimodal nanostructured metals

Numerical investigation of fracture behavior of nanostructured Cu with bimodal grain size distribution

Achieving High Strength and High Ductility in Nanostructured Metals: Experiment and Modelling

Computer Simulation of Strength and Ductility of Nanotwin-Strengthened Coarse-Grained Metals

Coordinated grain boundary deformation governed nanograin annihilation in shear cycling

Atomic scale studies of spall behavior in nanocrystalline Cu

Spallation Characteristics of Single Crystal Aluminum with Copper Nanoparticles Based on Atomistic Simulations

Sudden change of spall strength induced by shock defects based on atomistic simulation of single crystal aluminum

Spallation fracture dependence on shock intensity and loading duration in single-crystal aluminum

Understanding the spall behaviors of single crystalline aluminum under double decaying shock loadings: Atomistic simulations and theoretical models

Shock response of gradient nanocrystalline CoCrNi medium entropy alloy

Enhanced spall strength of single crystal aluminum by temperature rise mitigation and structural phase transition under shock pulse

Diffusive crack-grain interplay in freestanding nanocrystalline silver thin film

Influence of the twin boundary and Cr segregation on the spalling of Ni-base alloys by large-scale molecular dynamic simulations

Toughening by nano-scaled twin boundaries in nanocrystals

Dislocation evolution and peak spall strengths in single crystal and nanocrystalline Cu

The Quasi-Coarse-Grained Dynamics Method to Unravel the Mesoscale Evolution of Defects/Damage during Shock Loading and Spall Failure of Polycrystalline Al Microstructures