High-Performance, Biobased, Degradable Polyurethane Thermoset and Its Application in Readily Recyclable Carbon Fiber Composites
Binbo Wang,Songqi Ma,Xiwei Xu,Qiong Li,Tao Yu,Sheng Wang,Shifeng Yan,Yanlin Liu,Jin Zhu
DOI: https://doi.org/10.1021/acssuschemeng.0c02330
2020-07-07
Abstract:Carbon fiber (CF) reinforced polyurethane (PU) composites have attracted increasing attention in recent years. It is still a challenge to recycle the CF reinforced composites, and there is no report on the recycling of CF from PU matrix. In this paper, for the first time, a readily recyclable CF reinforced PU composite was prepared based on a biobased acetal diol, 2-(4-hydroxy-3-methoxyphenyl)-1,3-dioxan-5-ol (HMDO). The acetal diol was synthesized from the lignin derivative vanillin and was used to react with hexamethylene diisocyanate trimer to prepare the PU thermoset (PU-HMDO). On account of the cleavable acetal groups, the PU-HMDO could be decomposed within 40 min in low-concentration acidic solution completely. In addition, the heterocyclic structures of acetal and isocyanurate resulted in excellent mechanical and thermal properties of PU-HMDO. The tensile strength was 68 MPa, the elongation at break was 7.9%, and the glass transition temperature (<i>T</i><sub>g</sub>) was 130 °C, which are comparable to those of a PU thermoset (PU-BPA) from commercially available diol bisphenol A (BPA). The thermal stability of PU-HMDO was even higher than that of PU-BPA. The PU-HMDO-based CF composite exhibited similar mechanical properties to the PU-BPA-based CF composite, and CF could be reclaimed with maintained microscale morphology, chemical structures, and mechanical properties under mild acid conditions. This work will open a door to develop readily recyclable PU-based CF composites.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c02330?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c02330</a>.TGA curve of PU-HMDO and the mixture obtained by rotary evaporation in the PU-HMDO preparation stage; illustration of PU-HMDO and PU-BPA; surface morphologies of CFRC and CF; gel content of PU-HMDO and PU-BPA; and the glass transition temperature (<i>T</i><sub>g</sub>) and the cross-link density (<i>v</i><sub>e</sub>) of PU-HMDO after the solvent resistance test (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c02330/suppl_file/sc0c02330_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology