Abstract:Using polyurethane foams integrated with phase change materials (PCMs) that take cooperative advantages of heat insulation and heat storage capacity can meet the demand for thermal comfort and energy conservation purpose in the buildings. One-shot synthesis method, a cost-effective method, was used in this study for fabrication of PU-PCM composite foams. It is ascertained that thermal regulation capacity of composite foams is facilely tunable as latent heat storage properties of composite foams containing 10–20 wt.% n-octadecane as PCM ranged from 17.72 J.g−1 to 34.51 J.g−1. Inclusion of PCM resulted in increasing the cell size of composite foams accompanied with reduced closed-cell content compared with those of pristine PU foam. However, as the PCM fraction increased, the cell size of composite foams tended to decrease. Given the fact that the geometry of foam cells determines specific compressive properties, specific compressive strength and modulus of PU foam dropped from 3.89 ± 0.20 kPa.m3.kg−1 and 77.48 ± 5.72 kPa.m3.kg−1 to 2.67 ± 0.43 kPa.m3.kg−1 and 46.05 ± 9.86 kPa.m3.kg−1, respectively after incorporation of 10 wt.% n-octadecane. However, as the foam cell size reduced by increasing the PCM content, specific compressive strength and modulus were improved and reached 3.44 ± 0.30 kPa.m3.kg−1 and 65.50 ± 1.16 kPa.m3.kg−1, respectively for composite foam containing 20 wt.% n-octadecane which are comparable to those of PU foam. Additionally, the PCM leakage from this composite foam was less than others. This study suggests that by adjusting the PCM content, one-shot synthesized PU-PCM composite foams can provide not only reasonable thermal regulation properties and appropriate thermal reliability but also sufficient mechanical properties.

Preparation and characterization of oligomeric thermal phase change polyurethane foam

Synthesis and Thermal Performance of Polyurea Microcapsulated Phase Change Materials by Interfacial Polymerization

Preparation and characterization of polyurethane foams containing microencapsulated phase change materials for thermal energy storage and thermal regulation

Polyurethane Foam Containing Microencapsulated Phase-Change Materials with Styrene–divinybenzene Co-Polymer Shells

Development of smart polyurethane foam with combined capabilities of thermal insulation and thermal energy storage by integrating microencapsulated phase change material

Polyurethane/n-octadecane@silicon dioxide-polyhydroxyethyl methacrylate form-stable phase change materials with enhanced mechanical properties and thermal energy storage

Preparation and Properties of Phase‐change Heat‐storage UV Curable Polyurethane Acrylate Coating

Thermal energy storage and mechanical performance of composites of rigid polyurethane foam and phase change material prepared by one-shot synthesis method

Fabrication and Characterization of Polyurethane Foams Containing Phase Change Materials for Thermal Energy Storage

Preparation and structure-properties of crosslinking organic montmorillonite/polyurethane as solid-solid phase change materials for thermal energy storage

A New Strategy for Enhanced Latent Heat Energy Storage with Microencapsulated Phase Change Material Saturated in Metal Foam

Polyurethane Macro-Encapsulation For Ch3coona Center Dot 3h(2)O-Na2s2o3 Center Dot 5h(2)O/Melamine Sponge To Fabricate Form-Stable Composite Phase Change Material

Fabrication and Characterization of a Novel Polyurethane Microencapsulated Phase Change Material for Thermal Energy Storage

Effects of Microencapsulated Phase Change Materials Granularity and Heat Treat Treatment Condition on the Structure and Performance of Polyurethane Foams

Thermal Stability and Flame Retardancy of Rigid Polyurethane Foam Composites Filled with Phase-Change Microcapsule

Excellent interfacial compatibility of phase change capsules/polyurethane foam with enhanced mechanical and thermal insulation properties for thermal energy storage

Optimized emulsifier combination based microencapsulated phase change materials (MicroPCMs): Preparation, characterization, and applications

3D Shape-Stable Temperature-Regulated Macro-Encapsulated Phase Change Material: KAl(SO4)2·12H2O-C2H2O4·2H2O-CO(NH2)2 Eutectic/polyurethane Foam As Core and Carbon Modified Silicone Resin As Shell

Multiscale modeling of thermal properties in Polyurethane incorporated with phase change materials composites: A case study

A polyurethane solid–solid phase change material for flexible use in thermal management

Preparation and Thermal Properties of Microencapsulated Paraffin with Polyurea/acrylic Resin Hybrid Shells As Phase Change Energy Storage Materials