Study on the crystal structure of the rare earth oxyborate Yb26B12O57 from powder X-ray and neutron diffraction
Min Yang,Kuo Li,Jie Su,Q. Huang,Wei Bao,Liping You,Zhaofei Li,Yingxia Wang,Yu Jiang,Fuhui Liao,Jianhua Lin
DOI: https://doi.org/10.1016/j.jallcom.2011.01.098
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:Yb26B12O57, a rare earth oxyborate previously assigned as Yb3BO6, has been studied by various techniques including neutron and X-ray diffraction, 11B NMR spectroscopy, electron diffraction and high angle angular dark field-scanning transmission electron microscopy (HADDF-STEM). It crystallizes in the space group C2/m with cell parameters of a=24.5780(4)Å, b=3.58372(5)Å, c=14.3128(3)Å and β=115.079(1)°. The structure consists of slabs of rare earth sesquioxide and borate groups. The sesquioxide part is identified from the structural refinement, and is observed from HADDF-STEM image, while elucidation of borate groups is not straightforward. An additional oxygen atom (O31), which links two B2O5 groups into a B4O11 polyanion, is identified from the analysis of neutron diffraction data. The occupancy of this oxygen site is only quarter, which results in a random distribution of B4O11 and B2O5 groups along the b-direction. The chemical formula of ytterbium oxyborate is Yb26(BO3)4(B2O5)2(B4O11)O24, instead of the simple stoichiometric formula Yb3BO6. This compound is paramagnetic but its susceptibility deviated from the Curie–Weiss law at low temperature.