Abstract:Polyethylenes are currently the most prevalent synthetic polymers in the world, and the introduction of functional groups into polyethylene backbone can reduce problematic environmental persistence and enhance compatibility with other materials. This target can be addressed by transition-metal-catalyzed nonalternating copolymerization of ethylene with carbon monoxide, but it is generally impeded by the facile formation of alternating polyketones in kinetics. The reduction of carbonyl density in polyketones could weaken their inter-chain dipolar interaction, thus gradually approaching to polyethylene materials in term of crystalline and tensile properties. In this contribution, we communicate our continued efforts to investigate on the electronic and steric nature of Ni- and Pd-coordinated cationic [P,O] type catalysts, and they were used for nonalternating carbonylative copolymerization of ethylene, which resulted carbonyl functionalized polyethylenes with comparable molecular weight and desirable mechanistic property similar to those of commercial high-density polyethylene, and the incorporated carbonyls in polyethylene chains impart photodegradability. Notably, Pd complex 5 with an electron donating substituent on phosphine moiety yielded polyethylene products with a uniform dispersion of isolated carbonyls and a high molecular weight of ∼100 kg/mol.

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to introduce carbonyl functional groups into the polyethylene (PE) backbone through Ni - and Pd - diphospholene monoxide (PNPO) - catalyzed non - alternating copolymerization, in order to reduce the persistence of polyethylene in the environment and improve its compatibility with other materials. Specifically, the paper focuses on how to copolymerize ethylene with carbon monoxide (CO) through transition - metal - catalyzed non - alternating copolymerization to prepare polyethylene materials with a lower carbonyl density. These materials not only retain the crystallinity and tensile properties of traditional high - density polyethylene (HDPE), but also possess photodegradability due to the introduction of low - density carbonyls. ### Main research contents: 1. **Catalyst selection and design**: - The influence of the electronic and steric properties of Ni - and Pd - diphospholene monoxide (PNPO) catalysts on the copolymerization reaction was studied. - The activity and selectivity of the catalysts were optimized by changing the electron - donor and - acceptor groups on the catalysts. 2. **Non - alternating copolymerization reaction**: - Polyethylene materials with uniformly dispersed isolated carbonyls were successfully prepared by the non - alternating copolymerization method. - The effects of different reaction conditions (such as temperature, pressure, and CO content) on the polymer molecular weight, carbonyl content, and its distribution were investigated. 3. **Material performance evaluation**: - The crystallinity, melting point, and mechanical properties of carbonyl - functionalized polyethylene were evaluated by means of wide - angle X - ray diffraction (WAXD), differential scanning calorimetry (DSC), and mechanical tests. - The results show that the crystallinity and mechanical properties of these materials are similar to those of commercial high - density polyethylene, and they also possess photodegradability. ### Key findings: - **High molecular weight and low carbonyl density**: - The polyethylene material prepared using the Pd - 5 catalyst (with a strong electron - donor group) has uniformly dispersed isolated carbonyls and a molecular weight of up to 100 kg/mol. - The crystallinity and mechanical properties of this material are comparable to those of commercial high - density polyethylene, but it has photodegradability due to the introduction of low - density carbonyls. - **Influence of reaction conditions**: - Temperature and pressure have a significant impact on the activity of the polymerization reaction and the carbonyl content of the product. A higher temperature is beneficial for reducing the incorporation of CO and forming more isolated carbonyls. - A moderate CO content (0.2 mol%) can effectively promote the non - alternating copolymerization reaction to produce carbonyl - functionalized polyethylene with ideal properties. ### Significance: - **Environmental protection**: - By introducing carbonyl functional groups, the prepared polyethylene materials possess photodegradability, which helps to reduce the long - term accumulation of plastic waste in the environment and alleviate environmental pollution. - **Material properties**: - These carbonyl - functionalized polyethylene materials retain the excellent properties of traditional polyethylene and also possess new functional characteristics, and are expected to be applied in multiple fields. In conclusion, through systematic research, this paper shows how to achieve the functional modification of polyethylene materials through catalyst design and optimization, providing new ideas for the development of environmentally - friendly high - performance plastics.

Carbonyl Functionalized Polyethylene Materials via Ni- and Pd-diphosphazane Monoxide Catalyzed Nonalternating Copolymerization

Studies on Alternating Copolymerization of Ethylene and Carbon Monoxide Using Nickel‐Based Catalyst: Cocatalyst and the Polarity of Solvent

Preparation Of Comb-Shaped Polyolefin Elastomers Having Ethylene/1-Octene Copolymer Backbone And Long Chain Polyethylene Branches Via A Tandem Metallocene Catalyst System

Pinwheel-Shaped Tetranuclear Organoboron Catalysts for Perfectly Alternating Copolymerization of CO2 and Epichlorohydrin.

Cationic Palladium Catalyzed Nonalternating Copolymerization of Ethylene with Carbon Monoxide: Microstructure Analysis and Computational Study

Preparation of Polyethylene Elastomers with Increased High Molecular Weight and Nearly Perfect Strain Recovery by Steric Control of Asymmetric Α-Diimine Nickel Catalyst

Scalable Nickel Catalysts for Carbonylative Terpolymerization of Ethylene/α-Olefin with High Efficiency

Functionalized semi‐crystalline polyethylene with polar groups at branch end enabled by bulky cationic palladium catalysts

Polyethylene materials with in-chain ketones from nonalternating catalytic copolymerization

Synthesis of Nonalternating Polyketones Using Cationic Diphosphazane Monoxide-Palladium Complexes

Combination of 8‐aminoquinoline Nickel Dichloride and Cp2ZrCl2 Catalysts for Ethylene Polymerization

Polyethylene Materials with In-Chain Ketones from Catalytic Copolymerization

Efficient Copolymerization of Ethylene with Polar Divinyl Monomer by Phosphino‐Phenolate Nickel Catalyst

Facile access to diverse polyethylenes via neutral salicylaldiminato nickel catalysts

Benchtop-Stable Carbyl Iminopyridyl NiII Complexes for Olefin Polymerization

Exploring steric effect of electron-donating group in palladium and nickel mediated ethylene polymerization and copolymerization with polar monomers

Recent Advancements in Mechanistic Studies of Palladium- and Nickel-Catalyzed Ethylene Copolymerization with Polar Monomers

Material Properties of Functional Polyethylenes from Transition-Metal-Catalyzed Ethylene–Polar Monomer Copolymerization

Aqueous Keto-Polyethylene Dispersions from Catalytic Copolymerization of Ethylene and Carbon Monoxide in Water

Keto-Polyethylenes with Controlled Crystallinity and Materials Properties from Catalytic Ethylene–CO–Norbornene Terpolymerization

Robust and Reactive Neutral Nickel Catalysts for Ethylene Polymerization and Copolymerization with a Challenging 1,1-Disubstituted Difunctional Polar Monomer