THE PAVEMENT PERFORMANCE AND LIFE-CYCLE COST IMPACTS OF CARBON FIBER MODIFIED HOT MIX ASPHALT

B. Wiljanen

Abstract:Hot mix asphalt (HMA) roadway repair and maintenance encompasses thousands of miles in the United States and all over the world. A better performing, longer lasting HMA pavement benefits all parties involved. Technologies to lengthen time between needed repair intervals and decrease maintenance costs are welcomed and being researched. One new technology in HMA pavements is carbon fibers. Carbon fibers, if successfully introduced into HMA pavement, may provide performance benefits and qualities to benefit intelligent transportation systems (ITS). Advancements in carbon fiber production, resulting in improved carbon fiber properties, add to the economic and performance attractiveness. Laboratory testing can be utilized as an indicator for field performance before possibly spending excess money in production. Performance predictions are made in three of HMA’s failure mechanisms which are thermal cracking, fatigue cracking, and permanent deformation. Another mechanism, reflective cracking, will also be examined although laboratory testing is not currently directly related to field performance. Field and laboratory specimens were manufactured for laboratory testing. Variations in mixture types included binder contents, binder types, and carbon fiber percentages. Results of this research are: • Asphalt binder testing (such as the dynamic shear rheometer, bending beam rheometer, and direct tensile tester) was difficult to perform due to the irregularities in test specimens caused by the carbon fiber. • Asphalt content had more influence than carbon fiber content on results in the low temperature performance utilizing the indirect tensile test. • The addition of carbon fibers at a percentage of 0.50% by mass of asphalt binder combined with a 0.1% increase in optimum asphalt binder content is economically attractive in fatigue analysis. • An economical analysis in permanent deformation data comparing a mixture with 0.50% carbon fiber by mass of asphalt binder at a 0.1% increase in optimum asphalt binder content versus a mixture with an increase in high temperature binder grade due to binder modification would be of interest.

Engineering,Materials Science,Environmental Science