Water-Based Polymer Colloids with a Branched Chain Architecture as Low-Gel Pressure-Sensitive Adhesives

Emily May Brogden,Stefan A. F. Bon

DOI: https://doi.org/10.1039/d4py00522h

IF: 4.6

2024-06-21

Polymer Chemistry

Abstract:The performance of water-based acrylic pressure-sensitive adhesives, in which the latex particles had minimal gel content of typically less than a few percent and the polymer chains had a branched architecture, were investigated. A series of semi-batch emulsion copolymerizations of 2-octyl acrylate, isobornyl acrylate and acrylic acid was carried out in the presence of ethylene glycol dimethacrylate as crosslinker. The molecular weight distributions and branched chain topology were regulated by using 2-ethylhexyl thioglycolate as a chain-transfer agent. The momoners and chain-transfer agent were selected as these were already available as bio-based feedstocks, or had a realistic potential to become available from non-petrochemical resources. Adhesive films cast from the polymer dispersions demonstrated good peel, shear strength and tack adhesion energies. This is attributed to polymer chain branching, which unlocks a broader window for the design rules for pressure-sensitive adhesives. Detailed rheological studies of the viscoelastic materials were conducted to support the adhesive test results.

polymer science

What problem does this paper attempt to address?

Based on the provided text, this paper attempts to address the issue of developing a water-based polyacrylate dispersion pressure-sensitive adhesive (PSA) with low gel content while maintaining good adhesive performance. Specifically, the researchers aim to achieve a low-gel-content water-based polyacrylate dispersion by introducing an appropriate amount of crosslinking agents and chain transfer agents to adjust the branching structure of the polymer chains. This dispersion should be able to match the adhesive performance of traditional high-gel-content PSAs.

The core objectives of the paper include:
1. **Reducing gel content**: By optimizing the branching structure of the polymer chains, reduce the gel content to improve the sustainability and recyclability of the material.
2. **Maintaining or improving adhesive performance**: Ensure that the low-gel-content water-based polyacrylate dispersion exhibits good performance in terms of peel strength, shear strength, and tack.
3. **Using bio-based monomers**: Explore the use of bio-based monomers (such as 2-octyl acrylate and isobornyl acrylate) to replace petroleum-based monomers, thereby enhancing the environmental friendliness of the material.

Through these objectives, the researchers hope to provide new ideas and technical solutions for developing more sustainable and environmentally friendly pressure-sensitive adhesives.