The Design and Preparation of Permittivity-Adjustable FeNi@SrFe-MOF Composite Powders
Zhifen Yuan,Donghan Jiang,Lei Chen,Zhenghou Zhu
DOI: https://doi.org/10.3390/coatings14010112
IF: 3.236
2024-01-16
Coatings
Abstract:When the thickness of the wave-absorbing material is low, there exists the problem of the narrow wave-absorbing frequency band, making it difficult to regulate the position of the wave-absorbing peak. In this study, FeNi@SrFe-MOF composite powders were synthesized using a hydrothermal method and a liquid-phase reduction method. The composite powder was spherical, with a particle size of about 50 μm–60 μm; the core layers of the powders were porous SrFe-MOF powders with permanent magnetization, and the outer layers were FeNi alloy nano-powder coatings with a particle size of 100 nm–120 nm, which took into account both the soft magnetization and the permanent magnetization properties of the composite powders. Additionally, a directional magnetic field was applied to the powder coating. By regulating the intensity and direction of the magnetic field, the electromagnetic parameters of the composite powder coating underwent sensitive changes, allowing for the precise regulation of the electromagnetic wave absorption performance of the composite powders. With the increase in magnetic field intensity, the ε′ value decreased significantly. The ε′ values were 8.56–7.35 for H453mT and 6.73–6.12 for H472mT. When no magnetic field was applied, the Snoke limit frequency of the μ′ value was 6.0 GHz. When the magnetic field intensity increased, the Snoke limit frequency of the μ′ value increased from 6.0 GHz, without the magnetic field, to 8.3 GHz; the Snoke limit of the composite powders was shattered. After the H453mT magnetic field regulation treatment, the powder coating exhibited good impedance matching characteristics with air. When the magnetic field intensity was 453mT and the thickness of the composite powders coating was 3.5 mm, the composite powders coating showed the strongest absorption peak when the R-value was −59 dB at 7.8 GHz, and the effective absorption bandwidth reached 3.2 GHz, exhibiting superb absorbent qualities. The wave absorption property of the coating can be sensitively changed by the magnetic field regulation treatment at the condition without changing the powder structure or coating structure, which provides a new strategy for the regulation of the wave absorption property and has broad application prospects.
materials science, multidisciplinary,physics, applied, coatings & films