Abstract:Reinforced concrete is one of the most commonly used materials in the construction industry. The most and main causes of reinforcement corrosion in concrete structures are chloride attack and carbonation. Many studies have been carried out in this field so far, but due to the multitude of influencing factors and their complexity, different results have been obtained. In this study, reinforced concrete samples were prepared and investigated to monitor the threshold of chloride concentration for corrosion of SD345 carbon steel rebar using the electrochemical impedance spectroscopy (EIS) and half-cell potential (HCP) tests. A series of electrolyte solutions containing different NaCl contents, that is, 0, 1, 2 and 3 wt%, were used to simulate the chloride environment. Given that the HCP values are relatively low for carbon steel rebars, there are a high possibility for corrosion of all samples. By increasing the NaCl content in electrolyte solution, the current density values were increased from the early stages, indicating corrosion enhancement in the samples with increasing chloride ions in solution. The EIS results show that resistance of passive film gradually decreased by increasing the chloride concentration which shows that non-protective corrosion and porous products have been advanced on the surface of steel rebar. Furthermore, the EIS findings indicated an obviously increase of charge transfer resistance and a clearly reduction in the non-ideal interfacial capacitance after 16 weeks exposed to 2 wt% NaCl solution which can be attributed to the high degree of hydration and the efficiently refined the pore structure of the reinforced concretes. Scanning electron microscopy analysis confirmed the results obtained by electrochemical experiments.

Corrosion Resistance of Cr-bearing Rebar in Simulated Concrete Pore Solutions

Corrosion Resistance of Cr-bearing Rebar in Concrete with Chloride Ion Content

Corrosion Behavior of Cr/RE Alloyed Rebar in Carbonated Simulated Concrete Pore Solutions with Chloride Ions

Effect of Chromium Micro-alloying on the Corrosion Behavior of a Low-carbon Steel Rebar in Simulated Concrete Pore Solutions

Corrosion Resistance of Cr-bearing Rebar to Macrocell Corrosion Caused by Concrete Cover Crack

Pitting Corrosion Behaviour of New Corrosion-Resistant Reinforcement Bars in Chloride-Containing Concrete Pore Solution

Influence of Threshold Chloride Concentration on Corrosion Behavior of Low-Alloy Steel Rebar in Concrete Pore Solutions

The Electrochemical Characterization of Rebar Passivation Film in Simulated Concrete Media

Modified passivity and pitting corrosion resistance of a corrosion-resistant rebar in carbonated concrete pore solutions with different contents of carbonate/bicarbonate ions

Enhanced Corrosion Resistance of Reinforcing Steels in Simulated Concrete Pore Solution with Low Molybdate to Chloride Ratios

Corrosion Behavior of Steel Rebars in Historical Reinforced Concrete Structures Submitted to Chlorides in the Simulated Concrete Pore Solution

Corrosion Resistance of a Cr-Bearing Low-Alloy Reinforcing Steel: Effect of Surface Condition, Alkaline Solution, and Chloride Content

Corrosion Behavior of Cr-Ni Alloyed Corrosion Resistant Rebar in Chloride Environment

Chloride Resistance of Cr-bearing Alloy Steels in Carbonated Concrete Pore Solutions

Threshold Chloride Concentration of Stainless Steels in Simulated Concrete Pore Solution

Threshold Level of Chloride Ions for Corrosion of SD345 Carbon Steel Reinforcement in Concrete

Corrosion Behavior of Cr Micro-alloyed Corrosion-resistant Rebar in Neutral Cl − -Containing Environment

Corrosion Resistance of Fine-Grained Rebar in Simulated Concrete Pore Solutions by Means of Electrochemical Methods

Chloride-induced Corrosion Resistance of Low-Alloyed Reinforcement Steels in Two Different Ph Simulated Concrete Solution

Corrosion Behavior and Durability of Low-Alloy Steel Rebars in Marine Environment

Chloride-induced Corrosion Patterns of Reinforcements in Simulated Pore Solutions of Calcium Sulfoaluminate Cement Concrete: an Analytical Study