Research on variation in nanopore parameters and surface characteristics of anodic aluminum oxide (AAO) films with time-controlled anodization processes
Jisoo Kim,Chanyoung Jeong
DOI: https://doi.org/10.1007/s10853-024-09806-y
IF: 4.5
2024-06-08
Journal of Materials Science
Abstract:The lightweight, recyclable aluminum alloy with the "green metal" modifier enhances energy efficiency by substituting various metals; however, its thin natural oxide layer is susceptible to cracking or corrosion in harsh environments, requiring surface treatment, such as anodization. Anodization improves metal's corrosion and wear resistance, hardness, and esthetic impression. Its arrangement of the nanopore structure influences the uniformity of secondary processes, such as coloring, paint, and coating adhesion. This study applied time variables to the three-step process's first anodization and anodic aluminum oxide (AAO) removal steps to confirm AAO pore uniformity. A six-hour anodization formed 8.26 ± 0.10 μm thick AAO. Subsequent removal steps, lasting 0.5, 2, 6, and 10 h, resulted in a 5.04 μm h −1 AAO removal rate. As the AAO removal time increased, pore diameter ( D p ) and interpore distance ( D int ) changed, and the 6 h AAO removal condition was used for anodization. The AAO's pore uniformity, surface roughness, and wettability were observed after the first anodization for 1, 3, 5, 7, and 9 h; AAO removal; and second anodization. Furthermore, larger, uniform pores formed as the first anodization time increased, and pore structure changes increased AAO's roughness and decreased contact angle. This study introduces an efficient anodization manufacturing method that can be employed across various fields, aiming to enhance material stability and improve energy storage efficiency.
materials science, multidisciplinary