Abstract:Hard carbon (HC) stands out as the preeminent anode material for sodium-ion batteries (SIBs) which are deployed in expansive energy storage infrastructures. Herein, the large enough graphene nanosheets interlayer and abundant nanopores with a diameter of ∼2.1 nm induced by adjusting the pyrolysis temperature in the thermosetting phenolic resin-derived hard carbon matrix to augment the performance of the sodium ion storage. The presence of sufficiently large carbon interlayers has been proven to provide active sites for reversible adsorption, enabling effective storage of sodium ions in the high-voltage slope region, while also promoting rapid Na + transport. Meanwhile, forming abundant closed nanopores with larger sizes helps sodium ion storage in the low-voltage plateau region. In the optimized samples, the formation of sufficient long graphene nanosheets with a perfect crystal lattice, which further shrinks to form enclosed nanopores, effectively reduces defective sites and specific surface area. Additionally, the appropriate content of C-O and C=O functional groups contributes to an exceptional initial Coulombic efficiency (ICE) of up to 93%. Simultaneously, the optimized sample HC-1500 contributes to a remarkable plateau capacity of 294 mAh g - 1 during the charging process (high reversible capacity of 403 mAh g - 1 at 0.1 C). Moreover, based on the microstructure evolution and Na storage behavior of hard carbon, an "adsorption (27%) – filling (73%)" sodium storage mechanism that the sodium storage as a quasi-metallic sodium state is demonstrated. Consequently, this study will offer valuable insights for the development of hard carbon anodes tailored for high-energy practical SIBs, while also advancing the understanding of sodium storage mechanisms.

Porous Hard Carbon Derived from Walnut Shell as an Anode Material for Sodium-Ion Batteries

Curly hard carbon derived from pistachio shells as high-performance anode materials for sodium-ion batteries

N, S self‐doped porous carbon with enlarged interlayer distance as anode for high performance sodium ion batteries

Biomass‐Derived Phosphorus‐Doped Porous Hard Carbon Anode for Stable and High‐Rate Sodium Ion Batteries

Lotus Seedpod-Derived Hard Carbon with Hierarchical Porous Structure as Stable Anode for Sodium-Ion Batteries

High temperature induced abundant closed nanopores for hard carbon as high-performance sodium-ion batteries anodes

Hard Carbon Microsphere with Expanded Graphitic Interlayers Derived from a Highly Branched Polymer Network as Ultrahigh Performance Anode for Practical Sodium-Ion Batteries

Sycamore fruit seed‐based hard carbon anode material with high cycle stability for sodium‐ion battery

A porous biomass-derived anode for high-performance sodium-ion batteries

Biomass-derived hard carbon material for high-capacity sodium-ion battery anode through structure regulation

Exploring Carbonization Temperature to Create Closed Pores for Hard Carbon As High-Performance Sodium-Ion Battery Anodes

Sulfur and phosphorus co-doped hard carbon derived from oak seeds enabled reversible sodium spheres filling and plating for ultra-stable sodium storage

Porous hard carbon spheres derived from biomass for high-performance sodium/potassium-ion batteries

Hierarchical porous hard carbon derived from rice husks for high-performance sodium ion storage

Scalable synthesis of N/S co-doped hard carbon microspheres as a high-performance anode material for sodium-ion batteries

Hard Carbon Reprising Porous Morphology Derived from Coconut Sheath for Sodium-Ion Battery

Hard carbon derived from waste tea biomass as high-performance anode material for sodium-ion batteries

Pomegranate Peel-Derived Hard Carbons as Anode Materials for Sodium-Ion Batteries

Hard Carbon/graphene Microfibers As a Superior Anode Material for Sodium-Ion Batteries

From Natural Fibers to High-Performance Anodes: Sisal Hemp Derived Hard Carbon for Na-/K-Ion Batteries and Mechanism Exploration

Hard Carbon Derived for Lignin with Robust and Low-Potential Sodium Ion Storage