Mussel-inspired biocompatible polydopamine/carboxymethyl cellulose/polyacrylic acid adhesive hydrogels with UV-shielding capacity

Zuwu Tang,Yanan Miao,Jing Zhao,He Xiao,Min Zhang,Kai Liu,Xingye Zhang,Liulian Huang,Lihui Chen,Hui Wu

DOI: https://doi.org/10.1007/s10570-020-03596-7

IF: 6.123

2021-01-02

Cellulose

Abstract:Hydrogels are attractive due to their various applications in the fields of biomedical materials, cosmetics, and biosensors. To enhance UV protection and prevent skin penetration behaviors, inspired by the mussel adhesive proteins, the functional polydopamine (PDA) is employed herein to fabricate polydopamine/carboxymethyl cellulose/polyacrylic acid (PDA/CMC/PAA) adhesive hydrogels. To disperse PDA nanoparticles well in the PAA matrix, dopamine was self-polymerized in CMC solution to form PDA/CMC complex. Acrylic acid was polymerized in PDA/CMC complex solution and cross-linked to construct UV-resistant PDA/CMC/PAA hydrogel. The morphology, rheological behavior, mechanical properties and adhesion strength of PDA/CMC/PAA hydrogels were studied by scanning electron microscopy, rotational rheometer, universal test machine. Owing to the hydrogen bonding interaction between the PDA/CMC complex and PAA, the PDA/CMC/PAA hydrogels showed high resilience and compressive strength to withstand large deformation. The hydrogels exhibited strong adhesion to various substrate surfaces, such as stainless steel, aluminum, glass and porcine skin. The biocompatibility and UV-shielding properties were investigated through culture of cells and UV irradiation test. The adhesiveness of PDA promoted cell adhesion and provided the PDA/CMC/PAA hydrogels good biocompatibility with 96% of relative cell viability. The hydrogels possessed excellent UV-shielding ability to prevent collagen fibers from being destroyed during UV irradiation, which has promising potential in the practical applications for UV filtration membrane and skin care products.

materials science, textiles,polymer science, paper & wood

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop a multifunctional hydrogel with ultraviolet (UV) protection ability. This hydrogel can not only provide effective UV shielding but also maintain good biocompatibility and strong adhesion to different surfaces. Specifically, the researchers used mussel - inspired dopamine (PDA), carboxymethyl cellulose (CMC) and polyacrylic acid (PAA) composites to prepare a new type of PDA/CMC/PAA adhesive hydrogel. This hydrogel aims to overcome the potential toxicity, photodegradation and photocatalytic effects of existing UV - protection materials (such as organic filters and inorganic particle filters), while enhancing the mechanical properties, adhesion strength and biocompatibility of the materials, making it have broad application prospects in sun - protection films and skin - care products.

### Key problems solved in the paper:
1. **UV protection**: By introducing PDA, the hydrogel can effectively absorb UV rays and prevent UV damage to the skin.
2. **Biocompatibility**: The PDA/CMC/PAA hydrogel shows good cell compatibility, with a relative cell survival rate as high as 96%, which is suitable for products in direct contact with the skin.
3. **Adhesion performance**: The hydrogel shows strong adhesion to various surfaces such as stainless steel, aluminum, glass and pigskin. In particular, the adhesion strength to stainless steel reaches 780 ± 50 kPa, much higher than that of ordinary PAA hydrogels.
4. **Mechanical properties**: The hydrogel has high elasticity and compressive strength and can return to its original state under large deformation, showing excellent mechanical properties.

### Experimental methods:
- **Material preparation**: The PDA/CMC complex was formed by self - polymerizing dopamine in the CMC solution, and then acrylic acid monomers were added for cross - linking to finally prepare the PDA/CMC/PAA hydrogel.
- **Performance testing**: It includes the characterization of UV - shielding performance, biocompatibility, adhesion strength, mechanical properties and other aspects.

### Results and discussion:
- **UV - shielding performance**: The PDA/CMC/PAA hydrogel shows significant UV - absorption ability in the wavelength range of 200 - 600 nm, and the UV - absorption ability increases with the increase of PDA content.
- **Biocompatibility**: The high biocompatibility of the hydrogel to NIH 3T3 cells was confirmed by MTT assay and cell morphology observation.
- **Adhesion performance**: The hydrogel shows excellent adhesion performance to various surfaces, especially the adhesion strength to stainless steel is much higher than that of other materials.
- **Mechanical properties**: The hydrogel has high elasticity and compressive strength and can still maintain relatively high mechanical properties after multiple compression - unloading cycles.

In conclusion, through the design and preparation of the PDA/CMC/PAA hydrogel, this paper has successfully solved the deficiencies of existing UV - protection materials and demonstrated its potential application value in sun - protection films and skin - care products.