High-Throughput Preparation and Mechanical Property Screening of Zr-Ti-Nb-Ta Multi-Principal Element Alloys via Multi-Target Sputtering

Haochen Qiu,Xuehui Yan,Shuaishuai Wu,Wei Jiang,Baohong Zhu,Shengli Guo
DOI: https://doi.org/10.3390/coatings13091650
IF: 3.236
2023-09-21
Coatings
Abstract:Zr-Ti-Nb-Ta alloys were synthesized in parallel via multi-target co-sputtering deposition with physical masking in a pseudo-ternary Ti-Nb-ZrTa alloy system. Sixteen alloys with distinct compositions were obtained. Comprehensive characterization of phase structure, microstructure, Young's modulus, and nanoindentation hardness was undertaken. The Ti-Nb-ZrTa alloys exhibited two typical phase structures: a single-BCC solid-solution structure, and an amorphous structure. Nanoindentation quantification confirmed a Young's modulus ranging from 110 to 130 GPa, alongside nanoindentation hardness spanning 3.6 to 5.0 GPa. The combination of good hardness and a relatively low Young's modulus renders these alloys promising candidates for excellent biomedical materials. This work not only offers an effective method for the high-throughput synthesis of multi-principal element alloys, but also sheds light on a strategy for screening the phase structure and mechanical performance within a given alloy system.
materials science, multidisciplinary,physics, applied, coatings & films
What problem does this paper attempt to address?
This paper aims to address the application of multi-principal element alloys (MPEAs) in the field of biomedical materials. Specifically, researchers have parallelly prepared 16 different compositions of alloys in a pseudo-ternary Ti-Nb-Zr-Ta alloy system using multi-target co-sputtering deposition technology, and comprehensively characterized their phase structure, microstructure, Young's modulus, and nanoindentation hardness. These Ti-Nb-Zr-Ta alloys exhibit two typical phase structures: a single body-centered cubic (BCC) solid solution structure and an amorphous structure. Quantified by nanoindentation, the Young's modulus of these alloys ranges from 110 to 130 GPa, and the nanoindentation hardness ranges from 3.6 to 5.0 GPa. The good hardness and relatively low Young's modulus make these alloys potential excellent biomedical materials. Moreover, this work not only provides an efficient high-throughput synthesis method for multi-principal element alloys but also reveals strategies for screening phase structures and mechanical properties within a specific alloy system.