Effect of variations in proportions of CNC/TiO2 reinforcements on performance of biodegradable hybrid nanocomposites

Shubham Kumar Gupta,Alok Kumar Trivedi,M. K. Gupta

DOI: https://doi.org/10.1007/s13399-024-06337-z

IF: 4.05

2024-11-27

Biomass Conversion and Biorefinery

Abstract:The present work aims to enhance the performance of PLA-based hybrid composite films by changing the proportions of reinforcing particles. Firstly, PLA bionanocomposite films were prepared with varying weight percentages (1, 3, and 5) of crystalline nanocellulose (CNC), and its tensile test was carried out to obtain the optimal concentration for maximum strength. The maximum tensile strength was seen for the film with 1 wt% concentration of CNC, which was 9.41% higher than that of pure PLA film. Thereafter, the PLA-based hybrid nanocomposite films with varying proportions of CNC and TiO 2 nanoparticles at optimal concentrations of reinforcement were prepared through the solvent casting method. A positive effect of the hybridization of CNC and TiO 2 nanoparticles was seen on the performance of biodegradable PLA films. The XRD analysis revealed that the crystalline nature of nanocomposite films was significantly affected by the addition of CNC and TiO 2 , and the maximum crystallinity index was obtained at 90.10% for the film CNC (C100 T0). Further, the tensile properties of nanocomposite films were found to be considerably improved with the addition of CNC and TiO 2 . The maximum strength was observed for (C75T25) nanocomposite film, which was 31.76% higher than the neat PLA film. The statistical analysis was performed to analyze significant differences in tensile strength among the hybrid nanocomposite films and it was seen that tensile strength differences between samples were statistically significant. It was also observed that the incorporation of nanoparticles decreased the penetration resistance and water contact angles of the hybrid nanocomposite films.

energy & fuels,engineering, chemical