Abstract:The augmented finite element method (A-FEM) is used to study the fundamental composite failure problem of delamination and associated damage events spreading from a stress concentrator during tensile loading. The solution exploits the ability of A-FEM to account for coupled multiple crack types that are not predetermined in shape or number. The nonlinear processes of each fracture mode are represented by a cohesive model, which provides a unified description of crack initiation and propagation and can also describe crack coalescence and bifurcation. The study problem is an orthogonal double-notched tension specimen, in which delaminations interact with transverse ply cracks, intra-ply splitting cracks, non-localized fine-scale matrix shear deformation, and fiber breaks. Cohesive laws and constitutive laws for matrix shear deformation are calibrated using literature data from independent tests. The calibrated simulations are mesh independent and correctly reproduce all qualitative aspects of the coupled damage evolution processes. They also correctly predict delamination sizes and shapes, the density of transverse ply cracks, the growth rate of splitting cracks, softening of the global stress–strain curve, and the ultimate strength. A sensitivity analysis relates variability in cohesive law parameters to predicted deviance in engineering properties. Given the known variability in cohesive law parameters, the predicted deviance in ultimate strength agrees with that in experimental data. The importance of including the interactions between different crack systems and non-localized shear deformation is demonstrated by suppressing the presence of separate mechanisms; the predicted delamination shapes, splitting crack growth rate, and the stress–displacement relationship fall into significant error.

Buckling variability analysis in damaged composite laminates subjected to thermally varying environment

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Uncertain buckling characteristics of thermally loaded and internally defected variable fiber spacing composite laminates

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

Analysis of Cord-Rubber Composite Response Using the Nonlinear Continuum Damage Mechanics Approach

Continuum damage mechanics based failure prediction and damage assessment in laminated composite structures

Numerical simulation and experiment validation of variable stiffness composite laminates with open holes under unidirectional tension

High-fidelity Simulations of Multiple Fracture Processes in a Laminated Composite in Tension

Linear Static Behavior of Damaged Laminated Composite Plates and Shells

Failure analysis and experimental study on bolted composite joints based on continuum damage mechanics

A novel damage characterization approach for laminated composites in the absence of material and structural information

Predicting delamination in composite structures

Microscopic Progressive Damage Simulation and Scale-Span Analysis of Cross-Ply Laminate Based on the Elastic–Plastic Theory

A parametric study on the buckling of functionally graded material plates with internal discontinuities using the partition of unity method

A novel FFT framework with coupled non-local elastic-plastic damage model for the thermomechanical failure analysis of UD-CF/PEEK composites

Simulation and analysis of delamination damage propagation in CFRP structures

A non-linear Ritz method for progressive failure analysis of variable angle tow composite laminates

Thermo-Mechanical Post Buckling Analysis of Multiwall Carbon Nanotube-Reinforced Composite Laminated Beam under Elastic Foundation

Numerical Analysis for Damage Detection in CFRP Bolted Joints Using Strain Measurement

Damage Evolution and Multi-Scale Analysis of Carbon Fiber-Reinforced Cross-Ply Laminate with Thermal Residual Stress

Progressive Failure Analysis of Composite Laminates Subjected to Transverse Loading with Augmented Finite Element Method