Modification of mixed-halide quasi-2D perovskites by aminophylline towards efficient and spectrally stable blue light-emitting diodes with low efficiency roll-off

Xingxing Duan,Bufan Yu,Guangrong Jin,Dengliang Zhang,Jiangshan Chen,Dongge Ma

DOI: https://doi.org/10.1039/d4tc04214j

IF: 6.4

2024-11-06

Journal of Materials Chemistry C

Abstract:Blue perovskite light-emitting diodes (PeLEDs) based on the quasi two-dimensional (quasi-2D) perovskites with chloride (Cl) and bromine (Br) ions have made significant progress in improving external quantum efficiencies (EQEs) during the past few years. However, the mixed-halide quasi-2D PeLEDs still suffer from the issues of serious efficiency roll-off and spectral instability. Here, the modification of mixed-Cl/Br quasi-2D perovskites with a multi-functional additive was proposed to achieve efficient blue PeLEDs with reduced efficiency roll-off and stable electroluminescence (EL) spectra. Aminophylline (AMP) with Lewis base characteristics was employed as the additive to incorporate with the CsPb(Cl/Br) 3 based quasi-2D perovskites. It was observed that the introduction of AMP additive suppressed the low dimensional phases in the quasi-2D blue perovskite film, leading to that carriers can be harvested for radiative recombination rather than be located at the low dimensional phases. In addition, the AMP additive, containing carbonyl and imine groups, can coordinate with the uncoordinated Pb 2+ , which enables the passivation of defects and the reduction of trap-assisted non-radiative recombination in the blue quasi-2D perovskite films. As a result, based on the AMP-modified quasi-2D perovskites, the champion PeLED achieved a maximum EQE of 13.2% with the stable EL peak at 484 nm, which is 1.6 times of the pristine device without AMP additive. Importantly, the AMP-modified blue PeLEDs remained the EQE of as high as 11.5% at the high luminance of 1000 cd m −2 , demonstrating a significantly reduced EQE roll-off. Meanwhile, the AMP-modified devices presented more stable spectra than the pristine devices under various voltages or continuous operation at an identical initial luminance. This study demonstrated a facile modification strategy by using a multi-functional additive to facilitate the improvement of efficiency roll-off and spectral stability in mixed-Cl/Br quasi-2D blue PeLEDs.

materials science, multidisciplinary,physics, applied