Abstract:High silicon and molybdenum (SiMo) ductile iron is commonly used for car exhaust systems, and its micro-structural dispersity depends on intrinsic parameters, which include alloy composition and inoculation efficiency, as well as extrinsic factors, such as casting wall thickness and molding material, which define cooling rate during solidification. Micro-structural dispersity is referred to as the degree of heterogeneity of sizes of structural constituencies within the microstructure. A variation in the micro-structural dispersity could impact the high temperature performance of SiMo ductile iron during static oxidation and transient thermo-mechanical loading conditions. In this study, static high temperature tests were performed on SiMo ductile iron solidified in a casting with varying wall thicknesses from 5 mm to 100 mm. The faster solidified specimens (taken from near chilled casting surfaces) had extremely high micro-structural dispersity as compared to the thicker section samples. After thermal exposure, each of the samples were characterized using 2D sections and 3D μCT images, and the results indicated an order of magnitude difference in graphite phase dispersity. The surface degradation was quantified after static oxidation experiments were implemented at temperature intervals between 650 °C and 800 °C. Non-destructive μCT 3D analysis and SEM/EDS were performed on cross sections and used to quantify the scale topology and structure. Carbon analysis was used to decouple the scale formation and decarburization phenomena that occurred within the samples. These methods enabled the quantification of the oxidation of the SiMo cast iron with different micro-structural dispersity levels after being exposed to high temperature static oxidation. Additionally, the complex material behavior during oxidation-assisted transient thermo-mechanical loading will be presented in a separate article.

Electrical properties of thermal oxide scales on pure iron in liquid lead-bismuth eutectic

Oxygen-iron interaction in liquid lead-bismuth eutectic alloy

Effect of Silicon and Aluminum Addition on Corrosion Behavior of ODS Iron-Based Alloys in Liquid Lead–Bismuth Eutectic

Fretting behavior of oxide scale formed on ferritic/martensitic steel after pre-exposure to lead-bismuth eutectic

Experimental and Theoretical Analysis for Hypoeutectic Cast Iron Oxidation Behaviors

Investigation of Selective Oxidation During Cooling of Hot-Rolled Iron-Manganese-silicon Alloys

Wetting and Spreading Behavior of Molten Iron in Contact with Graphite Substrate: Interfacial Effects

Lamellar Spacing Characteristics of Eutectoids in Oxide Scale Formed on Iron After Holding at 300–500℃

Corrosion Behaviors of Thermally Grown Oxide Films on Fe-based Bulk Metallic Glasses

First-principles study on the corrosion resistance of iron oxide surface and grain boundary in austenitic steel to lead–bismuth eutectic

Influence of Interface Electric Field on Interaction Between Molten Iron and Refractory Interface

EIS analysis on the anodic dissolution kinetics of pure iron in a highly alkaline solution

Effect of Micro-Structural Dispersity of SiMo Ductile Iron on High Temperature Performance during Static Oxidation

Critical behaviour in the transport properties of pure iron

Long-Term Behaviors of Oxide Layer in Liquid Lead–Bismuth Eutectic (LBE), Part II: Model Applications

Influence of temperature on the microstructural evolution of SIMP and T91 steels in liquid lead-bismuth eutectic: Experiments and molecular dynamics simulations

Redox-structure dependence of molten iron oxides

Interfacial microstructure and corrosion behavior of ODS FeCrAl alloy in oxygen-saturated lead-bismuth eutectic at 450 °C

Effect of post-annealing on the oxidation behavior of hot rolled ODS-FeCrAl steel in liquid lead

Liquid metal embrittlement susceptibility of an oxide-dispersion strengthened FeCrAl alloy in contact with liquid lead-bismuth eutectic at 350 °C

Experimental Liquidus Studies of the Pb-Fe-Ca-O System in Air