Anion Doping for Layered Oxides with a Solid-Solution Reaction for Potassium-Ion Battery Cathodes
Yan-Song Xu,Mu-Yao Qi,Qing-Hua Zhang,Fan-Qi Meng,Yong-Ning Zhou,Si-Jie Guo,Yong-Gang Sun,Lin Gu,Bao-Bao Chang,Chun-Tai Liu,An-Min Cao,Li-Jun Wan
DOI: https://doi.org/10.1021/acsami.2c00811
2022-03-10
Abstract:The development of potassium-ion batteries (PIBs) is challenged by the shortage of stable cathode materials capable of reversibly hosting the large-sized K+ (1.38 Å), which is prone to cause severe structural degradation and complex phase evolution during the potassiation/depotassiation process. Here, we identified that anionic doping of the layered oxides for PIBs is effective to combat their capacity fading at high voltage (>4.0 V). Taking P2-type K2/3Mn7/9Ni1/9Ti1/9O17/9F1/9 (KMNTOF) as an example, we showed that the partial substitution of O2– by F– enlarged the interlayer distance of the K2/3Mn7/9Ni1/9Ti1/9O2 (KMNTO), which becomes more favorable for fast K+ transition without violent structural destruction. Meanwhile, based on the experimental data and theoretical results, we identified that the introduction of F– anions effectively increased the redox-active Mn cationic concentration by lowering the average valence of the Mn element, accordingly providing more reversible capacity derived from the Mn3+/4+ redox couple, rather than oxygen redox. This anionic doping strategy enables the KMNTOF cathode to deliver a high reversible capacity of 132.5 mAh g–1 with 0.53 K+ reversible (de)intercalation in the structure. We expect that the discovery provides new insights into structural engineering for pursuing stable cathodes to facilitate the future applications of high-performance PIBs.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.2c00811.Experimental section, figures showing TEM images, XPS results, XRD patterns, charge/discharge curves, CV curves, theoretical calculation results, tables showing element content, and crystallographic parameters (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology