Abstract:3D hollow ZIF-67 MOF based photocatalyst with excellent photo-catalytic performance was synthesized.The @TiO2 sample exhibited strongest photo-current intensity.The photodegradation kinetic follows the Langmuir-Hinshelwood (L-H) model.Superoxide free radicals (•O2−) and hydroxyl radicals (•OH) were the primary and secondary reactive species during photo-degradation.Photocatalytic technology is considered the most promising green technology for the degradation and removal of organic pollutants. In this paper, an innovative multifunctional photocatalytic material has been successfully prepared. The zeolitic-imidazolate-framework-67 (ZIF-67) was first synthesized by an easy and green approach. Then, a polydopamine (PDA) mid-layer was incorporated on its surface via dopamine self-polymerization, which not only serves as a stable linking agent, but also increases the amount of visible light captured and reduces the recombination of photogenerated electron-hole pairs. After the hydrolysis and hydrothermal process of tetrabutyl orthotitanate, the TiO2 nanoparticles were uniformly grafted on the surface, and finally, the hollow @TiO2 was successfully obtained. The prepared @TiO2 photocatalyst was characterized by various techniques, and further used for the photo degradation of a variety of dyes in wastewater in the presence of visible light. A degradation rate of almost 100% was achieved for Acid Fuchsin and Congo Red within 40 min, followed by Erythrosine B and Rose Bengal with a 99% degradation rate within 150 min. Moreover, the ZIF-67-based photocatalyst exhibited high stability and recyclability and maintained an excellent photocatalytic performance during continued cycling. Furthermore, the superoxide radical (•O2−) and the hydroxyl radical (•OH) were the primary and secondary reactive species during photodegradation. Overall, the excellent performance of this simple photocatalyst was clearly demonstrated, and its numerous advantages, such as low energy consumption, low cost, non-toxicity, and environmental friendliness, showing promising potential for its practical implementation.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1876107021001279-fx1_lrg.jpg">Download : Download high-res image (143KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1876107021001279-fx1.jpg">Download : Download full-size image</a></li></ol>

Facile room temperature synthesis of ZIF-67 for efficient photocatalytic degradation of methylene blue under sunlight irradiation

Insight into the Novel Z-Scheme ZIF67/WO3 Heterostructure for Improved Photocatalytic Degradation of Methylene Blue Under Visible Light

Photocatalytic Degradation of Methylene Blue by Engineering Tungstic Acid@ZIF‐67 Cocatalyst

Easy Preparation of Zinc Molybdate Photocatalyst and Its Application for Degradation of Methylene Blue

ZIF-67 with Argon annealing treatment for visible light responsive degradation of organic dyes in a wide pH range

Strategic combination of metal–organic frameworks and C3N4 for expeditious photocatalytic degradation of dye pollutants

Enhanced Visible-Light-driven Photocatalytic Removal of Refractory Pollutants by Zn/Fe Mixed Metal Oxide Derived from Layered Double Hydroxide

Molecularly Imprinted Polymer-Based Photocatalyst for Highly Selective Degradation of Methylene Blue.

Surface induced growth of ZIF-67 at Co-layered double hydroxide: Removal of methylene blue and methyl orange from water

Solar Assisted Removal of Methylene Blue Dye from Wastewater Using Zinc-Metal Organic Framework (Zn-MOF)

Enhanced photo-catalytic efficiency through dual-functional ZIF based materials: Fabrication and application as a degradation of organic dyes

ZIF-67/BiOCl Z-Scheme Heterojunction Photocatalyst for Photodegradation of Organic Dyes and Antibiotics

Photocatalytic degradation of methylene blue and methyl orange in a Zn(II)-based Metal–Organic Framework

Microwave-assisted synthesis of ZnO structures for effective degradation of methylene blue dye under solar light illumination

Synthesis of a silica matrix with ZnO nanoparticles for the fabrication of a recyclable photodegradation system to eliminate methylene blue dye

The Development and Synthesis of a CdZnS @Metal–Organic Framework ZIF-8 for the Highly Efficient Photocatalytic Degradation of Organic Dyes

Facile fabrication of ternary CuO/CuS/ZnS for photodegradation of methylene blue

Preparation and performance of scalable photocatalyst beads: A case study of tetracycline degradation assisted by visible light and peroxymonosulfate activation

Facile synthesis of activated carbon/ZnFe2O4 hybrid composite as an efficient photocatalyst for enhanced degradation of methylene blue (MB) and reactive red 120 dye under UV light

Crystallinity regulation of ZIF-67 via defective MgO layer made by high voltage-assisted oxidation approach for optimal 4-nitrophenol reduction

Facile Synthesis of ZIF-67 for the Adsorption of Methyl Green from Wastewater: Integrating Molecular Models and Experimental Evidence to Comprehend the Removal Mechanism